Abstract:Alloying and nanostructuring are two strategies used to facilitate the efficient electrocatalysis of the oxygen reduction reaction (ORR) by Pt, where the high index surfaces (HISs) of Pt exhibit superior activity for ORR. Here, we report the fabrication of PtCu3 nanodendrites possessing rich spiny branches exposing n(111) × (110) HISs. The dendrites were formed through an etching-modulated seeding and growing strategy. Specifically, an oxidative atmosphere was initially applied to form the concaved nanocubes of the Pt-Cu seeds, which was then switched to an inert atmosphere to promote an explosive growth of dendrites. Separately, the oxidative or inert atmosphere failed to produce this hyperbranched structure. Electrochemical dealloying of the PtCu3 nanodendrites produced Pt3Cu shells with Pt-rich surfaces where HIS-exposed dendrite structures were maintained. The resulting PtCu3@Pt3 nanodendrites in 0.1 M HClO4 exhibited excellent mass and area specific activities for ORR, which were 14 and 24 times higher than that of commercial Pt/C, respectively. DFT calculations revealed that Cu alloying and HISs both contributed to the significantly enhanced activity of Pt, and that the oxygen binding energy on the step sites of HISs on the PtCu3@Pt3 nanodendrites approached the optimal value to achieve a near peak-top ORR activity.Atmosphere-modulated synthesis followed by electrochemical dealloying produces exposed high index surfaces on the composition-graded nanodendrites of PtCu3@Pt3 to achieve mass and area activities of Pt that are respectively 14 and 24 times higher than that of pure Pt catalyst.

Wavy PtCu Alloy Nanowire Networks with Abundant Surface Defects Enhanced Oxygen Reduction Reaction

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Trimetallic Au@PtPd Mesoporous Nanorods As Efficient Electrocatalysts for the Oxygen Reduction Reaction

Zn-induced Defect Engineering to Activate Bimetallic NiCo Alloy@nitrogen-Doped Graphene Hybrid Nanomaterials for Enhanced Oxygen Reduction Reaction

Defect-rich ultrathin AuPd nanowires with Boerdijk–Coxeter structure for oxygen reduction electrocatalysis

Heterostructured Cu/CuO Nanoparticles Embedded within N-Doped Carbon Nanosheets for Efficient Oxygen Reduction Reaction

Strain-Modulated Platinum-Palladium Nanowires for Oxygen Reduction Reaction.

Pd@PtRuNi core–shell nanowires as oxygen reduction electrocatalysts

Cu-template-dependent synthesis of PtCu nanotubes for oxygen reduction reactions

Enhanced Electrocatalytic Performance of Ultrathin PtNi Alloy Nanowires for Oxygen Reduction Reaction

Engineering Platinum–nickel Nano-Alloys in Hierarchically Ordered Porous Cobalt-Nitrogen-doped Carbon for Highly Efficient Electrocatalytic Oxygen Reduction

Nanoporous Surface Alloys As Highly Active and Durable Oxygen Reduction Reaction Electrocatalysts

Monodispersed Sub-5.0 Nm PtCu Nanoalloys As Enhanced Bifunctional Electrocatalysts for Oxygen Reduction Reaction and Ethanol Oxidation Reaction

Surface-modulated palladium-nickel icosahedra as high-performance non-platinum oxygen reduction electrocatalysts.

Synthesis and Design of a Highly Stable Platinum Nickel Electrocatalyst for the Oxygen Reduction Reaction

Nanotubular Mesoporous PdCu Bimetallic Electrocatalysts toward Oxygen Reduction Reaction

Efficient Oxygen Reduction Reaction Using Mesoporous Ni-Doped Co3o4 Nanowire Array Electrocatalysts

High index surface-exposed and composition-graded PtCu3@Pt3Cu@Pt nanodendrites for high-performance oxygen reduction

Surface Engineering of Hierarchical Platinum-Cobalt Nanowires for Efficient Electrocatalysis

A General Method for Multimetallic Platinum Alloy Nanowires as Highly Active and Stable Oxygen Reduction Catalysts

Interlaced Pd-Ag Nanowires Rich in Grain Boundary Defects for Boosting Oxygen Reduction Electrocatalysis.