Dual Effect of Cu on the Al3Sc Nanoprecipitate Coarsening

Y. H. Gao,L. F. Cao,J. Kuang,J. Y. Zhang,G. Liu,J. Sun

DOI: https://doi.org/10.1016/j.jmst.2019.07.035

2019-01-01

Journal of Material Science and Technology

Abstract:It is generally considered that the Al 3 Sc nanoprecipitates are highly thermal stable, mainly due to quite slow Sc diffusion in the α-Al matrix. In this paper, we demonstrate in an Al-Cu-Sc alloy that the Cu atoms have dual effect on the coarsening of Al 3 Sc nanoprecipitates. On the one hand, the Cu atoms with high diffusivity tend to accelerate the Al 3 Sc coarsening, which results from the Cu-promoted Sc diffusion.On the other hand, some Cu atoms will segregate at the Al 3 Sc/matrix interface, which further stabilizes the Al 3 Sc nanoprecipitates by reducing the interfacial energy. Competition between these two effects is tailored by temperature, which rationalizes the experimental findings that the coarsening kinetics of Al 3 Sc nanoprecipitate is greatly boosted at 300℃-overaging while significantly suppressed at 400℃-overaging.