The effect of surfactant-free TiO2 surface hydroxyl groups on physicochemical, optical and self-cleaning properties of developed coatings on polycarbonate
A. Dayerizadeh,M. Mulaj,S. Han,M. Muschol,A. Takshi,S. Ma,H. Yaghoubi,X. Li,W. Gao
DOI: https://doi.org/10.1088/0022-3727/46/50/505316
2013-11-27
Abstract:TiO2 is a prototypical transition metal oxide with physicochemical properties that can be modified more readily through sol–gel synthesis than through other techniques. Herein, we report on the change in the density of the hydroxyl groups on the surface of synthesized surfactant-free TiO2 nanoparticles in water due to varying the pH (7.3, 8.3, 9.3 and 10.3) of the peroxotitanium complex, i.e. the amorphous sol, prior to refluxing. This resulted in colloidal solutions with differing crystallinity, nanoparticle size, optical indirect bandgaps and photocatalytic activity. It was shown that increasing the density of hydroxyl groups on TiO2 particles coupled with low-temperature annealing (90 °C) induced an anatase to rutile transformation. Increasing the pH of the peroxotitanium complex interrupted the formation of anatase phase in crystalline sol, as evidenced by intensity increases of the Raman bands at ∼822 (Ti–O–H) and 906 cm−1 (vibrational Ti–O–H) and an intensity decrease of the band at 150 cm−1 (anatase photonic Eg). Films prepared from higher pH suspensions showed lower roughness. The reaction rate constants for photo-induced self-cleaning activity of TiO2 films prepared from colloidal solutions at pH 7.3, 8.3, 9.3 and 10.3 were estimated at 0.017 s−1, 0.014 s−1, 0.007 s−1 and 0.006 s−1, respectively.
Chemistry,Physics,Materials Science