CoNi Alloy Nanoparticles Encapsulated in N-Doped Graphite Carbon Nanotubes as an Efficient Electrocatalyst for Oxygen Reduction Reaction in an Alkaline Medium
Lijuan Niu,Guohua Liu,Yifan Li,Jiawen An,Boyuan Zhao,Jingsu Yang,Dan Qu,Xiayan Wang,Li An,Zaicheng Sun
DOI: https://doi.org/10.1021/acssuschemeng.1c02098
2021-06-08
Abstract:Transition metal alloys and their compounds have been drafted as relatively economic and high-activity non-noble metal electrocatalysts for the oxygen reduction reaction (ORR). However, the stability of catalysts is regarded as a critical issue for practical application. Here, we report CoNi alloy nanoparticles embedded in a nitrogen-doped graphite carbon nanotube () electrocatalyst, which is synthesized from metal precursors and dicyandiamide nanofibers formed by freeze-drying pretreatment. The electrocatalyst exhibits remarkable ORR performance (a positive onset potential at 0.90 V vs reversible hydrogen electrode (RHE), a half-wave potential at 0.84 V vs RHE, and a high limiting current density (6.4 mA cm<sup>–2</sup>)) in an alkaline medium. The outstanding ORR catalytic behavior is attributable to the properties with a high specific surface area and the collaborative influence between a CoNi alloy and a nanotube protective layer. The also displays antimethanol toxicity and good stability over 10,000 cycles, attributed to the unique structure of N-GCNT that is more conducive to mass transfer and protects the alloy particles from corrosion under harsh conditions. This simple route can be widely used to prepare other alloy electrocatalysts with relatively economic value and high performance in power conversion and stockpile device fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c02098?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c02098</a>.Materials; catalyst preparation; electrochemical measurements; materials characterization; SEM and XRD of at 600–800 °C; CV and LSV curves of and ; H<sub>2</sub>O<sub>2</sub> percentage and electron transport number (<i>n</i>) of , , and ; LSV curves with or without 1 M methanol and before or after 10,000 cycles of ; LSV curves of commercial Pt/C before and after 10,000 cycles; TEM images after 10,000 cycles; XRD patterns after 10,000 cycles; XPS spectra after 10,000 cycles; table of the content of different types of N; list of the nonprecious alloy electrocatalysts in the ORR (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c02098/suppl_file/sc1c02098_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology