Photoinduced In Situ Spontaneous Formation of a Reduced Graphene Oxide-Enwrapped Cu–Cu 2 O Nanocomposite for Solar Hydrogen Evolution
Na Li,Wenjun Yan,Yu Niu,Shijie Qu,Pingping Zuo,Hongcun Bai,Ning Zhao
DOI: https://doi.org/10.1021/acsami.0c20636
2021-02-17
Abstract:The fast recombination of photogenerated charge carriers and poor stability have impeded the application of many narrow band gap semiconductors with otherwise excellent photocatalytic performance. A metal–semiconductor Schottky junction is a promising strategy to accelerate charge separation and enhance catalytic efficiency. However, the preparation of these structures often involves intricate processes and harsh conditions, which will inevitably destroy the electronic structures of the semiconductors and ruin their original properties in practical applications. In this study, a reduced graphene oxide (RGO)-enwrapped Cu–Cu<sub>2</sub>O nanocomposite (Cu–Cu<sub>2</sub>) spontaneously evolved from an aqueous alcoholic solution containing cupric ions and graphene oxide (GO) under simulated sunlight irradiation. During this process, GO reduction and Cu–Cu<sub>2</sub>O nanoparticles growth occurred simultaneously in conjunction with <i>in situ</i> RGO encapsulation. Benefiting from the superior intrinsic semiconductor characteristic retention under mild reaction conditions, strong component interactions, and efficient interfacial charge transfer, the distinctive Cu–Cu<sub>2</sub> nanocomposite supplied multiple channels for rapid electron transfer to substantially enhance the charge carrier separation efficiency and provide perfect chemical protection to effectively prevent Cu<sub>2</sub>O photocorrosion. This product also greatly suppressed self-aggregation to decrease the size of nanoparticles. Based on these merits, the Cu–Cu<sub>2</sub> nanocomposite offered promising advances in photoelectrochemical and photocatalytic H<sub>2</sub> evolution. This work provides an innovative photoinduced strategy for constructing an RGO-enwrapped semiconductor nanocomposite with efficient charge transfer interfaces while providing novel insights for the efficient solar energy utilization.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c20636?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c20636</a>.XPS characterizations of Cu, Cu–Cu<sub>2</sub>O, and Cu–Cu<sub>2</sub> nanocomposite (Figure S1); UV–visible absorption spectroscopy of Cu<sub>2</sub>O, Cu–Cu<sub>2</sub>O, and Cu–Cu<sub>2</sub> nanocomposite (Figure S2); electrochemical impedance spectroscopy of Cu<sub>2</sub>O, Cu–Cu<sub>2</sub>O, and Cu–Cu<sub>2</sub> nanocomposite (Figure S3); effect of copper ion concentration on photocatalytic H<sub>2</sub> evolution rate (Figure S4); effect of GO amount on photocatalytic H<sub>2</sub> evolution performance (Figure S5); effect of H<sub>2</sub>O<sub>2</sub> concentration on photocatalytic H<sub>2</sub> evolution rate (Figure S6); XRD patterns of the as-prepared Cu–Cu<sub>2</sub> nanocomposite under different concentrations of H<sub>2</sub>O<sub>2</sub> (Figure S7); XPS and TEM analysis of the obtained Cu–Cu<sub>2</sub> samples under different H<sub>2</sub>O<sub>2</sub> concentrations (Figure S8); XRD patterns and Cu 2p XPS narrow spectra of Cu–Cu<sub>2</sub> nanocomposite, Cu<sub>2</sub>O, and Cu–Cu<sub>2</sub>O before and after cycling stability test of photocatalytic H<sub>2</sub> evolution (Figures S9–S11), respectively; TEM images of Cu<sub>2</sub>O, Cu–Cu<sub>2</sub>O, and Cu–Cu<sub>2</sub> nanocomposite after cycling stability test of photocatalytic H<sub>2</sub> evolution (Figure S12); effect of hole scavenger types and glycol addition on photocatalytic H<sub>2</sub> evolution rate (Figure S13); apparent quantum efficiency calculations; fitted parameters of time-resolved photoluminescence (TRPL) spectra (Table S1); and summary of literature for photocatalytic H<sub>2</sub> evolution over different photocatalysts (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c20636/suppl_file/am0c20636_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology