Abstract:Three-dimensional needle carbon fibre reinforced carbon and silicon carbide dual matrix composite (C/C-SiC) is one of a new type of high performance brake material. The carbon fibre preform prepared by three-dimensional needling method was first densified by chemical vapour infiltration (CVI) to form porous carbon/carbon (C/C) composites. Then, the porous C/C composites were converted into C/C-SiC by liquid silicon infiltration (LSI), in which silicon carbide matrix was formed by reaction of carbon and melting silicon. The microstructure, mechanical properties and friction behaviour of C/C-SiC have been investigated. The results indicated that the composite was composed of 55 wt% C, 39 wt% SiC and 6 wt% Si. The density of C/C-SiC was 2.2 g cm(-3) with 6.4% open porosity. The C/C-SiC exhibited good mechanical properties, especially excellent toughness which can help to avoid catastrophic brittle fracture. The flexural and compressive strength can reach to 214.6 MPa and 271.0 MPa, respectively. In addition, C/C-SiC had excellent impact damage tolerance of 25.2 kJ m(-2). Compared to the self-friction, the C/C-SiC with steel opposing material shown higher static coefficient of friction (0.74) and better stability coefficient (0.28), while exhibited lower dynamic coefficient of friction (0.25), higher temperature of friction subsurface (444 degrees C), higher wear rate (2.88 mu m cycle(-1)). The main wear mechanism of the C/C-SiC composites with different opposing material both includes adhesion and oxidation abrasion. (C) 2012 Elsevier Masson SAS. All rights reserved.

Microstructure, Mechanical and Ablation Behaviour of C/SiC–Si with Different Preforms

Microstructure and mechanical properties of 3D needled carbon fibre reinforced carbon and silicon carbide composites

ABLATION PROPERTIES OF THREE DIMENSIONAL NEEDLED C/SiC COMPOSITES BY THE CHEMICAL VAPOR INFILTRATION

Mechanical Properties of a 3D Needled C/SiC Composite with Graphite Filler

Microstructures and properties of Si-Zr alloy based CMCs reinforced by various porous C/C performs

Effects of preform structures on the mechanical and ablation properties of C/ZrC-SiC composites

Microstructure, Thermophysical, and Ablative Performances of a 3D Needled C/C–SiC Composite

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF THREE-DIMENSIONAL NEEDLED C/SiC COMPOSITE

Microstructure and Compressive Behaviour of 3D Needled C/SiC Composites

Microstructure and Mechanical Properties of Three Dimensional Cf/SiC-ZrC-ZrB2 Composites Prepared by Reactive Melt Infiltration Method

Effects of Preform Structure on Microstructure and Mechanical Properties of C/SiC Composites Reinforced by Si3N4 Nanowires

Microstructures and Ablation Properties of C/C−SiC−ZrC Composites Prepared Using C/C Skeletons with Various Densities

Mechanical and ablation properties of 3D orthogonal woven C/C-SiC composite based on high-solid-loading slurry impregnation

Microstructures and Ablation Properties of Al-Si Modified C/C Composites Produced by the Reactive Melt Infiltration Method

Preparation and Tribological Properties of C Fibre Reinforced C/Sic Dual Matrix Composites Fabrication by Liquid Silicon Infiltration

Microstructure and Properties of Needle Punching Chopped Carbon Fiber Reinforced Carbon and Silicon Carbide Dual Matrix Composite

EFFECT OF C/C POROUS PREFORM ON THE MICROSTRUCTURE AND FLEXURAL STRENGTH OF C/C-SiC COMPOSITES

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Effect of SiC content on the mechanical behaviour of a three-dimensional needled C/SiC composite