Mutual Destabilization of Wide Bandgap Perovskite and PbI2 Inclusions through Interface Carrier Trapping
Yang Zhou,E Laine Wong,Giulia Folpini,Martina Zanolini,Jesús Jiménez‐López,Antonella Treglia,Annamaria Petrozza
DOI: https://doi.org/10.1002/adfm.202406317
IF: 19
2024-07-11
Advanced Functional Materials
Abstract:PbI2 is rich in hole traps whose energy level spreads within the bandgap of perovskite and has a loose layered structure, which can trap photogenerated holes and accommodate ions (A‐site cations and halides) from the perovskite, respectively. As a result, the photodegradation of PbI2 and mixed halide perovskites are both accelerated when they are interfaced. Lead halide perovskites (LHPs) are promising for versatile optoelectronic applications due to their tunable bandgap, but their photoinstability impedes the development. Lead iodide (PbI2) inclusions are commonly seen in LHPs, either formed during the fabrication of the thin film or during its degradation under external stimuli like heat and illumination. Here It is shown how the coexistence of these different phases mutually boost their photodegradation. It is demonstrated that the photodecomposition of PbI2 to form I2, and the photo‐induced halide segregation and decomposition of the mixed I─Br perovskite are both accelerated when they are interfaced. Such a mutual destabilization originates from the nature of PbI2, both because it is rich in hole traps whose energy level spreads within the bandgap of perovskite and because it has a loose layered structure. Thus it becomes a sink for both photocarriers (holes) and ions (A‐site cations and halides) transferred from the perovskite, respectively. It is shown that consistently reducing the PbI2 inclusions in the mixed I─Br perovskite thin film improves the solar cell stability substantially, extending, in the model devices, the operational time from ≈10 to 500 h under illumination.
materials science, multidisciplinary,nanoscience & nanotechnology,physics, applied,chemistry, physical, condensed matter