Two-stage Temperature Change Chrome Tanning: A More Sustainable Tanning Process

Hui Zeng,Weixing Xu,Jianfei Zhou,Bi Shi

2019-01-01

Abstract:Under the guidance of molecular simulation of Cr(III) species in water solution, a novel chrome tanning process, the two-stage temperature change chrome tanning, was developed. In stage I, the pickled cattle hide was first tanned by a small amount of chrome tanning agent under room temperature to obtain basic hydrothermal stability. Then, in stage II, the pre-tanned wet-blue was tanned again under a high temperature (>= 60 degrees C) to enhance the reactivity of Cr(III) with collagen fibers. The shrinkage temperature of crusts, the absorptivity of chrome tanning agent and fatliquoring agent, the mechanical property and surface morphology of crusts were characterized to evaluate the tanning effect. The results showed that when the dosage of chrome tanning agent in two stages was 2 wt% (tanned under room temperature) and 1 wt% (tanned under 60 degrees C), respectively, the best performances of crust were achieved. In these conditions, the shrinkage temperature of crust was 104.6 degrees C. The comprehensive absorptivity of chrome tanning agent reached up to 96.3%. The absorptivity of fatliquoring agent in wet-blue was 90.2%. The mechanical property and grain fineness of the crust were comparable to those of conventional chrome tanned crust with 6 wt% chrome tanning agent. As a result, an efficient and more sustainable chrome tanning process with less offer of chrome tanning agent was achieved.