Preparation of Layered Titanate Nanosheets and Study of Cs+ Adsorption Performance
Wanlei Geng,Debin Wang,Yinfeng Liu,Jialing Zhang,Limei Zhong,Runxiong Lin,Li Ding,Lianying Wu,Dianquan DONG
DOI: https://doi.org/10.2139/ssrn.4141971
2022-01-01
SSRN Electronic Journal
Abstract:A new type of cesium ion sieve H-CTO nanosheets were successfully synthesized by acid modification on the prepared precursor CTO. The H-CTO were characterized by electron microscope observation, X-ray diffraction, FT-IR spectroscopy, Raman spectroscopy, and Thermal gravimetric analysis. Based on the above analysis, showing that cesium adsorption involved the O−H bonds break of -OH groups and the formation of O−Cs bonds. Accordingly, the adsorption of Cs ions from aqueous solution onto H-CTO had been investigated under different conditions, including a variety of contact times, temperatures, initial Cs ion concentrations, pH levels, and interfering ions. Furthermore, the kinetics and thermodynamics of ion exchange were explored. In the early stages of the study, the exchange of cesium ions on H-CTO was rapid, and equilibrium was reached after two hours. The pseudo-second-order kinetic model for Cs + adsorption fitted better (R 2 > 0.994), indicating that cesium ion adsorption was chemical. According to the thermodynamic analysis, the adsorption of cesium on H-CTO was mainly monolayer and had a maximum adsorption capacity of 328.95 mg/g (Cs + 2 g/L, pH = 9). The H-CTO also showed good adsorption ability in the alkaline environment and had high Cs + selectivity in high concentration solutions of the monovalent cations. After five cycles, the adsorption capacity of H-CTO for Cs + was still above 280.66 mg/g. Therefore, H-CTO nanosheets have a wide application prospect in alkaline Cs + aqueous solutions or radioactive wastes.