Synthesis and characterization of lactic acid esterified starch by an in-situ solid phase method
Ping Li,Xiaoyu He,Yingfeng Zuo,Xianjun Li,Yiqiang Wu
DOI: https://doi.org/10.1016/j.ijbiomac.2019.11.171
IF: 8.2
2020-08-01
International Journal of Biological Macromolecules
Abstract:To improve the hydrophobicity and thermoplastic processability of starch, lactic acid esterified starch (LA-e-starch) was prepared by in-situ solid phase esterification with corn starch as the raw material and LA as the esterifying agent. Fourier transform infrared spectroscopy confirmed that the esterification reaction was successful. The optimal esterification efficiency of LA-e-starch was obtained when the LA proportion was 20% by mass, catalyst ratio at 3%, reaction temperature 80 °C and reaction time 2.5 h. LA-e-starch was characterized by scanning electron microscopy (SEM), contact angle (CA) analysis, X-ray diffractometry (XRD), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA) as well as its water absorption rate evaluated. Results showed that in-situ solid phase esterification mainly occurred on starch granule surfaces and did not destroy the starch granularity. LA-e-starch surfaces were covered with a layer of polylactic acid resin, which caused starch granules to stick together. The initial contact angle of LA-e-starch was clearly larger than that of native starch and the water absorption rate lower than native starch in a 168 h test time, which showed that esterification effectively improved the hydrophobicity of starch. This esterification destroyed the crystalline structure of starch to some extent, resulting in a crystallinity reduction to 25.16%. In addition, the gelatinization temperature and enthalpy were lower than those of native starch. XRD and DSC analyses indicated that esterification modification increased starch thermoplasticity. Also, LA-e-starch exhibited better thermal stability than native starch, from which it was inferred that this application of esterification could improve the thermoplastic processability of starch modify the interfacial compatibility between starch and polymer resins.
polymer science,biochemistry & molecular biology,chemistry, applied