Abstract:In order to achieve the compatibility between excellent mechanical properties and good electrical conductivity of Al-Mg-Si alloys, detailed investigation was carried out to understand the microstructure evolution and their influences on performances of different Al-0.7Mg-0.6Si-0.2Ce-X (XSc, Y and Zr) alloys prepared by casting, homogenization, hot extrusion, solution and aging treatments. Under aging state, Ce can form a large number of micron-sized AlCeSi and a few AlCeFeSi phase. The strength increased to 334 MPa as a result of decreased grain size and improved precipitation effect and the electrical conductivity increased up to 53.53%IACS because of lower solute Si atoms. The β’’ precipitates were coarsened and consequently the volume fracture was largely reduced due to the presence of Sc element, leading to the decreased strength of 311 MPa. The more solute Mg, Si and Sc atoms increased the degree of free electron scattering and the electrical conductivity decreased to 51.86%IACS. It is also found that Sc significantly enhanced the elongation of the alloy from 11.8% to 18.0%, which might be attributed to the formation of Al3Sc and (Al, Si)3Sc phases. The addition of Y raised the electrical conductivity of Al-Mg-Si-Ce alloy to 55.79%IACS by ameliorating the volume fraction and distribution of β’’ precipitates and decreasing the solute Si atoms. The co-addition of Sc and Y inherited the advantages of such two alloys. The ultimate tensile strength, elongation, electrical conductivity of Al-0.7Mg-0.6Si-0.2Ce-0.2Sc-0.1Y alloy processed by aging treatments is 336 MPa, 19.4% and 53.11%IACS, respectively.

Aging and recrystallization behavior of quaternary Al-0.25Zr-0.03Y-0.10Si alloy

Aging and Recrystallization Behavior of Precipitation Strengthened Al-0.25Zr-0.03Y Alloy

Effect of Si addition on the precipitation and mechanical/electrical properties of dilute Al-Zr-Sc alloys

Microstructural evolution and mechanical property of Al–Zr and Al–Zr–Y alloys

Precipitation Evolution of Al–Zr–Yb Alloys During Isochronal Aging

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Effects of Y addition on microstructure and properties of Al-Zr alloys

Thermal Stability and Crystallization Behavior of Al86Ni9Y5 Amorphous Alloys with Different Si Addition

Exploring the Local Structure of Molten Al-Zr-Y(Si) Alloys Using Ab Initio Molecular Dynamics

Structural and compositional evolution of Al3(Zr,Y) precipitates in Al-Zr-Y alloy

Effects of y additions on the precipitation and recrystallization of Al-Zr alloys

Effects of Si addition on properties and microstructure of CuCrZr alloy

Effect of the interfacial reaction of aluminum and yttrium oxide on aging behavior of aluminum–magnesium–silicon alloy reinforced with yttrium oxide modified sub-micron alumina

Effect of Yttrium Addition on Microstructure and Mechanical Properties of Sr-Modified Low-Si Cast Aluminum Alloy

Effect of Aging Treatment Temperature on Microstructure and Properties of Al-9.3Si-0.41Mg-0.2Zr-0.01Sr-0.08Ti-0.2Ce Cast Aluminum Alloy

The Alloying Effects of Ge and Si on Thermal Stability and Crystallization Behavior of Al-Y Binary Amorphous Alloys

Study of Deformation and Aging Behaviors of a Hot Rolled–quenched Cu–Cr–Zr–Mg–Si Alloy During Thermomechanical Treatments

Effect of minor Sc and Zr on recrystallization behavior and mechanical properties of novel Al–Zn–Mg–Cu alloys

Effect of Multistage Solid Solution Treatment on Microstructure and Properties of Al-6.5Si-5.5Cu-0.2Zr-0.01Sr-0.06Ti-0.2Y Alloy

Effect of Step Quenching and Zr Addition on the Microstructure and Mechanical Properties of Al-Mg-Si Alloy

Microstructure evolution and performances of Al-0.7Mg-0.6Si-0.2Ce-X (X Sc, Y and Zr) alloys with high strength and high electrical conductivity