Abstract:Emulsifier-free emulsion binary copolymerizations of styrene with four types of quaternary ammonium cationic monomers, diallyldimethylammonium chloride (DADMAC), (3-(methacryloylamino) propyl) trimethyl ammonium chloride (MAPTAC), (2-methacryloyloxy) ethyl) trimethyl ammonium chloride (MATMAC), and vinylbenzyl trimethyl ammonium chloride (VBTMAC), were conducted at 70 degrees C. 2, 2'-azobis (2-methylpropionamidine) dihydrochloride (V50) and potassium persulphate (KPS) were used as cationic and anionic initiator, respectively. Ternary copolymerizations were also carried out in the presence of acrylamide as a second comonomer. Monomer conversions were followed by ultraviolet spectroscopy and the polymer microparticles were characterized using photon correlation spectroscopy, electrophoresis, colloid titration, and scanning electron microscopy. The results indicated that VBTMAC and MATMAC were highly reactive in the copolymerization with styrene whereas the incorporation of DADMAC was slow. MAPTAC had an intermediate reactivity. Binary copolymerization with VBTMAC, MATMAC, and MAPTAC produced particles smaller in size, but higher in surface-charge density, than styrene homopolymer particles. However, significant agglomerates were detected in the VBTMAC and MATMAC-containing latexes. In contrast, DADMAC-containing polymer particles were almost identical to styrene particles. Continuous nucleation took place in the binary copolymerizations with VBTMAC and with MATMAC when using V50 initiator. In the case of using KPS, VBTMAC-containing particles grew continuously to a mean size much larger than the corresponding particles initiated by V50. The presence of acrylamide reduced DADMAC-containing particle size and diminished the agglomeration in the VBTMAC- and MATMAC-containing latexes. The results were interpreted via particle formation mechanism. (C) 2000 John Wiley & Sons, Inc.

Surfactant-free Emulsion Copolymerization of Styrene and a Cationic Comonomer with Two Positively Charged Groups

Ab Initio Emulsion and Miniemulsion Polymerization of Styrene Mediated by a Cyclohexenyl-Functionalized Amphiphilic RAFT Agent

Formation of Highly Monodispersed Emulsifier-Free Cationic Poly(methylstyrene) Latex Particles

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Model System for Surfactant-Free Emulsion Copolymerization of Hydrophobic and Hydrophilic Monomers in Aqueous Solution

Ultrasonically Irradiated Emulsion Polymerization of Styrene in the Presence of A Polymeric Surfactant

Synthesis of Sub-100 nm and Narrow Particle Size Distribution Cationic Latex by One-Step Emulsion Polymerization

In Situ Charge Neutralization-Controlled Particle Coagulation and Its Effects on the Particle Size Distribution in the One-Step Emulsion Polymerization

Large-scale and Narrow Dispersed Latex Formation in Batch Emulsion Polymerization of Styrene in Methanol–water Solution

Formation of Monodispersed Polymer Particles in Emulsifier-Free Emulsion Polymerization

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

Synthesis and Properties Study of the Uniform Nonspherical Styrene/Methacrylic Acid Copolymer Latex Particles

Emulsifier-free emulsion copolymerization of styrene with quaternary ammonium cationic monomers

Surfactant‐free Synthesis of Amphiphilic Copolymer of Poly(styrene‐co‐acrylamide) in Aqueous Emulsion with the Assistance of Ultrasound

Preparation of Monodisperse and Anion‐Charged Polystyrene Microspheres Stabilized with Polymerizable Sodium Styrene Sulfonate by Dispersion Polymerization

Kinetics and mechanism of emulsifier-free emulsion polymerization: Styrene/surface active ionic comonomer system

Synthesis of Large-Scale, Monodisperse Latex Particles Via One-Step Emulsion Polymerization Through in Situ Charge Neutralization

Preparation of polymeric/inorganic nanocomposite particles in miniemulsions: II. Narrowly size-distributed polymer/SiO2 nanocomposite particles

Ultrasonically Induced Microemulsion Polymerization of Styrene

Particle Nucleation under Critical Micelle Concentration (CMC) in Emulsion Polymerization of Styrene and Its application in High Solid Content Latex

Synthesis of Silanol-Functionalized Latex Nanoparticles through Miniemulsion Copolymerization of Styrene and γ-Methacryloxypropyltrimethoxysilane