Abstract:In this work, a durable superhydrophobic fabric was fabricated by using a facile UV-induced surface covalent modification strategy. 2-isocyanatoethylmethacrylate (IEM) containing isocyanate groups can react with the pre-treated hydroxylated fabric, producing IEM molecules covalently grafted onto the fabric's surface, and the double bonds of IEM and dodecafluoroheptyl methacrylate (DFMA) underwent a photo-initiated coupling reaction under UV light radiation, resulting in the DFMA molecules further grafting onto the fabric's surface. The Fourier transform infrared, X-ray photoelectron spectroscopy and scanning electron microscopy results revealed that both IEM and DFMA were covalently grafted onto the fabric's surface. The formed rough structure and grafted low-surface-energy substance contributed to the excellent superhydrophobicity (water contact angle of ~162°) of the resultant modified fabric. Notably, such a superhydrophobic fabric can be used for efficient oil–water separation, for example a high separation efficiency of over 98%. More importantly, the modified fabric exhibited excellent durable superhydrophobicity in harsh conditions such as immersion in organic solvents for 72 h, an acidic or alkali solution (pH = 1–12) for 48 h, undergoing laundry washing for 3 h, exposure to extreme temperatures (from −196° to 120°), as well as damage such as 100 cycles of tape-peeling and a 100-cycle abrasion test; the water contact angle only slightly decreased from ~162° to 155°. This was attributed to the IEM and DFMA molecules grated onto the fabric through stable covalent interactions, which could be accomplished using the facile strategy, where the alcoholysis of isocyanate and the grafting of DFMA via click coupling chemistry were integrated into one-step. Therefore, this work provides a facile one-step surface modification strategy for preparing durable superhydrophobic fabric, which is promising for efficient oil–water separation.

Preparation of Super Hydrophobic Mmos2/pdms Coating for Fabrics

Fabrication of Durable Superhydrophobic Coating on Fabrics Surface for Oil/water Separation

Feasible Fabrication of A Durable Superhydrophobic Coating on Polyester Fabrics for Oil-Water Separation

Superhydrophobic Al2O3/MMT-PDMS Coated Fabric for Self-Cleaning and Oil-Water Separation Application

Fabrication of Durable Superhydrophobic Surface for Versatile Oil/Water Separation Based on HDTMS Modified PPy/ZnO

Facile Process for the Fabrication of Durable Superhydrophobic Fabric with Oil/water Separation Property

Superhydrophobic mGO/PDMS hybrid coating on polyester fabric for oil/water separation

A Facile Approach to Fabricate the Durable and Buoyant Superhydrophobic Fabric for Efficient Oil/Water Separation

Versatile superhydrophobic bismuth molybdate cotton fabric for oil/water separation and decompose dyestuff

Vapor-Liquid Sol-Gel Approach to Fabricating Highly Durable and Robust Superhydrophobic Polydimethylsiloxane@Silica Surface on Polyester Textile for Oil-Water Separation

Superhydrophobic Cotton Fabric Coated With Tannic Acid/Polyhedral Oligomeric Silsesquioxane For Highly Effective Oil/Water Separation

Fabrication of Magnetically Inorganic/Organic Superhydrophobic Fabrics and Their Applications

Robust Superhydrophobic Fabric for Durability, Self‐Cleaning, and Oil/Water Separation Via Thiol–Acrylate Polymerization

UV-curable Superhydrophobic Organosilicon/silica Hybrid Coating on Cotton Fabric for Oil–water Separation

Stable and Durable Superhydrophobic Cotton Fabrics Prepared via a Simple 1,4‐Conjugate Addition Reaction for Ultrahigh Efficient Oil‐Water Separation

Facile UV-Induced Surface Covalent Modification to Fabricate Durable Superhydrophobic Fabric for Efficient Oil–Water Separation

Facile Preparation of Robust Superhydrophobic Cotton Textile for Self-Cleaning and Oil–Water Separation

Preparation of Superhydrophobic Materials for Oil/water Separation and Oil Absorption Using PMHS–TEOS-derived Xerogel and Polystyrene

Mussel-inspired chitosan modified superhydrophilic and underwater superoleophobic cotton fabric for efficient oil/water separation

Fabrication of Stable Superhydrophobic Coating on Fabric with Mechanical Durability, UV Resistance and High Oil-Water Separation Efficiency

PDMS-Based Hierarchical Superhydrophobic Fabric Coating Fabricated by Thermal Treatment and Electrostatic Flocking Technology