Abstract:One pot in situ preparation of poly(acrylic acid)-block-polystyrene (PAA-b-PSt) or poly(acrylic acid)-block-poly(acrylic acid-ran-styrene) (PAA-b-P(AA-r-St)) diblock copolymer nano-objects with multiple morphologies was developed through dispersion RAFT polymerization in ethanol/water mixtures mediated by hydrophilic poly(acrylic acid) (PAA)-based macromolecular RAFT agents. The polymerization shows characteristic features of living/controlled radical polymerization and the experimental results are confirmed by transmission electron microscopy (TEM), gel permeation chromatography (GPC), dynamic light scattering (DLS) and H-1 NMR. The effects of various parameters including the monomer conversion, St/AA feed ratio and solvent composition on the morphologies of PAA-b-PSt diblock copolymer nano-objects were investigated in detail. A faster polymerization rate was observed with increasing content of water in mixture solvents, and three stages with two clear turning points at which the rate was enhanced were observed during the polymerization process. Spherical micelles, worms, vesicles, and lacunal nanospheres have been obtained for PAA-b-PSt with the extension of the PSt block in 70/30, 80/20 and 90/10 w/w ethanol/water mixtures. Our results demonstrate that the interesting lacunal morphology of PAA-b-PSt diblock copolymer assembly can be successfully prepared and tuned at high styrene conversion. More interestingly, the residual AA, which was introduced to prepare the random P(AA-r-St) block, can promote the evolution of the copolymer aggregate morphology from spherical micelles to worms and pure vesicles in 90/10 and 80/20 w/w ethanol/water mixtures. The copolymerization of the residual hydrophilic monomer can be a convenient and effective method to tune the morphology and size of the block copolymer aggregates via polymerization-induced self-assembly (PISA). Finally, the in situ formation of silver/polymer composite nanoparticles was demonstrated, suggesting excellent applications in catalysis.

RAFT Dispersion Polymerization in the Presence ofBlock Copolymer Nanoparticles and Synthesis of Multicomponent BlockCopolymer Nanoassemblies

One-pot Synthesis of Octablock Copolymers of High-Molecular Weight Via RAFT Emulsion Polymerization

Synthesis of structured nanoparticles of styrene/butadiene block copolymers via RAFT seeded emulsion polymerization

In situ synthesis of diblock copolymer nano-assemblies via dispersion RAFT polymerization induced self-assembly and Ag/copolymer composite nanoparticles thereof

Precise evaluation of the block copolymer nanoparticle growth in polymerization-induced self-assembly under dispersion conditions

One-pot preparation of BAB triblock copolymer nano-objects through bifunctional macromolecular RAFT agent mediated dispersion polymerization

How the Polymerization Procedures Affect the Morphology of the Block Copolymer Nanoassemblies: Comparison Between Dispersion RAFT Polymerization and Seeded RAFT Polymerization

Synthesis of multicompartment nanoparticles of a triblock terpolymer by seeded RAFT polymerization

RAFT dispersion copolymerization of styrene and N-methacryloxysuccinimide: Promoted morphology transition and post-polymerization cross-linking

Synthesis of Multicompartment Nanoparticles of Block Copolymer through Two Macro-RAFT Agents Co-Mediated Dispersion Polymerization

Synthesis of Block Copolymer Nano-Assemblies Via ICAR ATRP and RAFT Dispersion Polymerization: How ATRP and RAFT Lead to Differences

Multiblock Poly(4‐vinylpyridine) and Its Copolymer Prepared with Cyclic Trithiocarbonate As a Reversible Addition–fragmentation Transfer Agent

Guidelines for the Synthesis of Block Copolymer Particles of Various Morphologies by RAFT Dispersion Polymerization.

From RAFT Emulsion Polymerization to RAFT Dispersion Polymerization: A Facile Approach to tune Dispersities and Self-assembled Behaviors of Block Copolymers

Dispersion Raft Polymerization Of 4-Vinylpyridine In Toluene Mediated With The Macro-Raft Agent Of Polystyrene Dithiobenzoate: Effect Of The Macro-Raft Agent Chain Length And Growth Of The Block Copolymer Nano-Objects

In-Situ Synthesis of Multicompartment Nanoparticles of Linear BAC Triblock Terpolymer by Seeded RAFT Polymerization

In situ synthesis of the Ag/poly(4-vinylpyridine)-block-polystyrene composite nanoparticles by dispersion RAFT polymerization

Self-Assembled Blends of Ab/Bab Block Copolymers Prepared Through Dispersion Raft Polymerization

Recent Advances in RAFT Dispersion Polymerization for Preparation of Block Copolymer Aggregates

In Situ Synthesis Of Nano-Assemblies Of The High Molecular Weight Ferrocene-Containing Block Copolymer Via Dispersion Raft Polymerization

Synthesis of diblock copolymer nano-assemblies by PISA under dispersion polymerization: comparison between ATRP and RAFT