Magnetostructural Coupling Induced Magnetocaloric Effects in Ni–Mn-Ga-Fe Microwires

Yanfen Liu,Lin Luo,Xuexi Zhang,Hongxian Shen,Jingshun Liu,Jianfei Sun,Ningning Zu

DOI: https://doi.org/10.1016/j.intermet.2019.106538

IF: 4.075

2019-01-01

Intermetallics

Abstract:Ferromagnetic shape memory Ni-Mn-Ga alloys exhibit magnetostructural coupling during the Curie points, which may alter their magnetocaloric effect (MCE). Here MCE of Ni-Mn-Ga alloy microwires are tuned by Fe doping. The chemical ordering annealed Ni49.6Mn25.5Ga22.6Fe2.3 (Fe-2), Ni49.6Mn25Ga21Fe4.4 (Fe4) and Ni48Mn26Ga19.5Fe6.5 (Fe6) microwires have diameters of similar to 30-50 mu m and grain sizes of similar to 2-5 mu m. The magnetic entropy changes (Delta S-m) of the microwires increase with external magnetic fields, then reach a positive peak and finally decrease to negative peak at a high field. The direct (negative Delta S-m, DMCE) and inverse (positive Delta S-m, IMCE) MCEs are attributed to microscopic and mesoscopic couplings in microwires. In addition, the specific features of MCEs are also controlled by the magnetization difference (Delta M) between martensite and austenite phases. Interestingly, the DMCE and IMCE are component dependent. At high Delta M, the linearly decreasing region is dominant and Fe4 and Fe6 microwires produce a negative Delta S-m at high magnetic fields due to the microscopic coupling with free electron valence ratio e/a = 7.692 and 7.725. On the other hand, the Delta M is small in Fe2 microwire, which has a positive Delta S-m because mesoscopic coupling is dominant with e/a = 7.607; the Delta S-m is highest when a single variant martensite occurs, then decreases linearly with increasing magnetic fields. The transition from positive to negative values in Delta S-m with the applied fields is related to the counterbalance of mesoscopic and microscopic couplings at e/a = 7.66.