Abstract:Inspired by nacreous architecture, the 2024Al/20-50 vol% B4C composites with a lamellar-interpenetrated structure were successfully manufactured via freeze casting and pressure infiltration, and the quasi-static and dynamic characteristics were conducted at strain rates ranging from 0.001 to 3000 s(-1). The strength of the composites enhanced as the strain rate increased up to 2000 s(-1) since the strain rate hardening effect facilitated the accumulation of dislocations. At the strain rate of 3000 s(-1), the adiabatic shear banding and its induced cracking were formed as the strengthening mechanisms were overcome by the thermal softening, which converted the dislocation structure from dislocation clusters to recrystallized grains, accompanied by a decrease in dislocation density, thereby degrading the compressive strength. A rigid network structure was formed in the composites with high particle content, and each particle had more inter-particle contact points, which made the strength of the composites increase with the increase of particle reinforcement content. This was also the reason why the strain rate sensitivity of the composites was considerably raised by introducing more particle reinforcement. However, increasing particle content heightened the composite susceptibility to strain localization and adiabatic shear damage, resulting in more brittleness of the 2024Al/50 vol% B4C composite at high strain rates. These findings could deepen the comprehension of the mechanical response and damage evolution of nacre-like composites exposed to extreme conditions and promote their applications.

Ballistic behavior and microstructure evolution of B4C/AA2024 composites

Experimental and Numerical Investigation on Ballistic Penetration Performance of TC4-Al3Ti Layered Composites by Hot Rolling

Analysis of morphology and microstructure of B 4 C/2024Al composites after 7.62mm ballistic impact

The Microstructure and Ballistic Performance of B4C/AA2024 Functionally Graded Composites with Wide Range B4C Volume Fraction

Influence of particulate B4C with high weight fraction on microstructure and mechanical behavior of an Al-based metal matrix composite

Ballistic Performance of B4C/Al2O3 Composite Ceramic Prepared by Reaction Sintering

Microstructure and wear properties of pressure infiltration B4Cp/2024Al composites

Interfacial Behavior and Damage Mechanism of Al-B4c/Al Laminated Composites under Ballistic Impact

The deformation of B4C particle in the B4C/2024Al composites after high velocity impact.

Residual microstructure and damage geometry associated with high speed impact crater in Al 2O 3 and TiB 2 particles reinforced 2024 Al composite

Investigation on microstructures and interface character of B4C particles reinforced 2024Al matrix composites fabricated by mechanical alloying

Spatial Span-Scale Microstructure Evolution and Ballistic Performance of Laminated Functionally Graded Composites of TiB2-Based Ceramic and Ti-6Al-4V Alloy

Mechanical Response and Damage Evolution of Bio-Inspired B4C-reinforced 2024al Composites Subjected to Quasi-Static and Dynamic Loadings

Residual microstructure associated with impact crater in Ti-6Al-4V meshes reinforced 5A06Al alloy matrix composite.

Microstructure and mechanical properties of B4C/2024Al functionally gradient composites

Microstructure and mechanical properties of in-situ B 4 C reinforced TC4 composites prepared by laser melting deposition

Research on Microstructure and Mechanical Properties of B<sub>4</sub>C/Al Composites by Liquid Mental Mixing

Influence of particulate B4C size on microstructural evolution and mechanical behavior in nanostructured Al matrix during heat treatment

Ballistic Performance and Mechanism of B4C/Al Laminated Targets with Different Configurations

Microstructure and mechanical properties of B 4C/AZ91 composites

Microstructure and Mechanical Properties of Al–B 4 C Composite at Elevated Temperature Strengthened with in Situ Al 2 O 3 Network