A strategy of optimizing magnetism and hysteresis simultaneously in Ni–Mn-based metamagnetic shape memory alloys
Hai-Le Yan,Xiao-Ming Huang,Jin-Han Yang,Ying Zhao,Feng Fang,Nan Jia,Jing Bai,Bo Yang,Zongbin Li,Yudong Zhang,Claude Esling,Xiang Zhao,Liang Zuo
DOI: https://doi.org/10.1016/j.intermet.2020.107063
IF: 4.075
2021-03-01
Intermetallics
Abstract:<p>Due to the existence of the magnetic-field-induced reverse martensitic transformation, the Ni–Mn–Z alloys where Z is the <em>p-block</em> element of In, Sn or Sb exhibit several state-of-the-art magnetoresponsive properties. From the perspective of practical application, a major challenge of this compound is to strengthen the ferromagnetism and reduce the transitional hysteresis ΔT<sub>Hys</sub> simultaneously. In this work, we report an alloying strategy to this issue, <em>i.e.</em>, the partial substitutions of Co and Cu for Ni and the <em>p-block</em> element, respectively, by a combined study of experiment and <em>ab-initio</em> calculation in the Ni<sub>45</sub>Co<sub>5</sub>Mn<sub>36</sub>In<sub>14–x</sub>Cu<sub>x</sub> (x = 0–1.5) alloys. Results show that the Cu replacement for the <em>p-block</em> element (In) can effectively reduce ΔT<sub>Hys</sub> owing to the improved geometrical compatibility between austenite and martensite. Moreover, the adopted alloying strategy of Cu hardly weakens the strong ferromagnetism of Ni(Co)–Mn–In, since the magnetism exhibits a weak dependence on the <em>p-block</em> element compared with Mn and Ni. The maximum reversible magnetic entropy change <span class="math"><math>ΔSMMax</math></span> of the Ni<sub>45</sub>Co<sub>5</sub>Mn<sub>36</sub>In<sub>13.3</sub>Cu<sub>0.7</sub> directionally solidified sample at a magnetic field of 5 T is 13.8 J·kg<sup>−1</sup>·K<sup>−1</sup>. The refrigeration capacity RC and effective refrigeration capacity RC<sub>eff</sub> equal to 473.7 J·kg<sup>−1</sup> and 270.2 J·kg<sup>−1</sup>, respectively. Both values belong to the highest one in the Ni–Mn-based alloys. Additionally, the working temperature window of the magnetocaloric effect is as wide as ~40 K. This work is expected to promote the design of advanced metamagnetic shape memory alloys.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering