Facile preparation of ultraviolet resistant “hard armors” on poly(p-phenylene benzobisoxazole) fibers through heat-induced surface treatment
Mengyuan Hao,Zhen Hu,Yonggang Zhang,Xin Qian,Li Liu,Jiaming Yang,Xuefei Wang,Jianhai Zhi,Yudong Huang,Xiaolu Shi
DOI: https://doi.org/10.1016/j.polymdegradstab.2022.109896
IF: 5.204
2022-05-01
Polymer Degradation and Stability
Abstract:In terms of high-performance organic fibers such as poly(p-phenylene benzobisoxazole) (PBO) fiber, anti-ultraviolet (UV) property is crucial for their applications in extreme conditions. In this work, excellent UV resistance was obtained through creating thermal oxidized PBO sheath on PBO fiber. In details, the peripheral UV sensitive oxazole groups were transformed into non-conjugated six membered rings after heat-induced gradient thermal oxidation, which could reduce UV sensitivity of PBO fiber and release energy produced by UV radiation through molecular vibration. The efficiency had been verified through UV-aging tests, and the results indicated that more than 90% of the fiber's tensile strength was retained and the surface defects after 800 h UV aging was also effectively decreased. There were also considerable improvement in mechanical properties of PBO fiber. For instance, the Young's modulus and compressive strength of PBO fiber increased by 33.5 % and 74%, respectively, along with the absence of yield zone. Meanwhile, the interfacial shearing strength (IFSS) of PBO reinforced epoxy resin composites increased by 64% with the introduction of non-conjugated structure. The inhomogeneous reduction in rigid-rod backbones resulted in the maintenance of internal microfibrils and decrease in peripheral microfibrils, and accordingly relieved the compressive damage. Enhancement of its interfacial property possibly resulted from increased surface roughness and decreased inert rigid-rod structure.
polymer science