Reduction of Ionic Silver by Sulfur Dioxide as a Source of Silver Nanoparticles in the Environment
Zhineng Hao,Fasong Li,Rui Liu,Xiaoxia Zhou,Yujing Mu,Virender K. Sharma,Jingfu Liu,Guibin Jiang
DOI: https://doi.org/10.1021/acs.est.0c08790
2021-03-08
Abstract:The natural formation of silver nanoparticles (AgNPs) <i>via</i> biotic and abiotic pathways in water and soil media contributes to the biogeochemical cycle of silver metal in the environment. However, the formation of AgNPs in the atmosphere has not been reported. Here, we describe a previously unreported source of AgNPs <i>via</i> the reduction of Ag(I) by SO<sub>2</sub> in the atmosphere, especially in moist environments, using multipronged advanced analytical and surface techniques. The rapid reduction of Ag(I) in the atmospheric aqueous phase was mainly caused by the sulfite ions formed from the dissolution of SO<sub>2</sub> in water, which contributed to the formation of AgNPs and was consistent with the Finke–Watzky model with a major contribution of the reduction–nucleation process. Sunlight irradiation excited SO<sub>2</sub> to form triplet SO<sub>2</sub>, which reacted with water to form H<sub>2</sub>SO<sub>3</sub> and greatly enhanced Ag(I) reduction and AgNP formation. Different pH values affected the speciation of Ag(I) and S(IV), which were jointly involved in the reduction of Ag(I). The formation of AgNPs was also observed in the atmospheric gas phase <i>via</i> direct reduction of Ag(I) by SO<sub>2</sub>(gas), which occurred even in 50 ppbv SO<sub>2</sub>(gas). The natural occurrence of AgNPs in the atmosphere may also be involved in silver corrosion, AgNP transformation and regeneration, detoxification of gaseous pollutants, and the sulfur cycle in the environment.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.0c08790?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.0c08790</a>.Identification and characterization of the formed AgNPs in the aqueous phase (Text S1); preparation of the stock solution with saturated SO<sub>2</sub>(gas) (Text S2); determination of SO<sub>4</sub><sup>2–</sup> by the IC method (Text S3); identification and characterization of the formed AgNPs in the gas phase (Text S4); absorption spectra of SO<sub>2</sub> solutions and the emission spectra of light sources (Figure S1); formation of AgNPs in the aqueous phase (Figure S2); production of SO<sub>4</sub><sup>2–</sup> from the reduction of Ag(I) by S(IV) in the aqueous phase (Figure S3); formation of AgNPs during the TEM characterization procedure (Figure S4); confirmation by LC-ICP-MS of the silver-containing nanoparticles in the gas phase (Figure S5); characterization of 40 nm PVP-capped AgNPs by SERS spectrum (Figure S6); SERS mapping of AgNPs formed in the gas phase (Figure S7); SERS mapping of AgNPs formed at different RHs (Figure S8); SERS mapping of AgNPs formed at different concentrations of SO<sub>2</sub>(gas) (Figure S9); mole fraction of sulfur(IV) species at equilibrium at different pH values (Figure S10); mole fraction of Ag(I) species at equilibrium at different pH values (Figure S11); and fitting results for the kinetics of Ag(I) reduction and AgNP formation (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.0c08790/suppl_file/es0c08790_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
environmental sciences,engineering, environmental