Synthesis Of Bi2wo6-X Nanodots With Oxygen Vacancies As An All-In-One Nanoagent For Simultaneous Ct/Ir Imaging And Photothermal/Photodynamic Therapy Of Tumors
Shun Wang,Han Wang,Cen Song,Zhicong Li,Zhaojie Wang,Hao Xu,Wanjian Yu,Chen Peng,Maoquan Li,Zhigang Chen
DOI: https://doi.org/10.1039/c9nr05236d
IF: 6.7
2019-01-01
Nanoscale
Abstract:All-in-one nanoagents with a single-component and all-required functions have attracted increasing attention for the imaging-guided therapy of tumors, but the design and preparation of such nanoagents remain a challenge. Herein, we report the introduction of oxygen vacancies to traditional semiconductors with heavy-metal elements for tuning photoabsorption in the near infrared (NIR) region, by using Bi2WO6 (band-gap: similar to 2.7 eV) as a model. Bi2WO6-x nanodots with sizes of similar to 3 or similar to 8 nm have been prepared by a facile coprecipitation-solvothermal method assisted by citric acid (CA, 0.1-1.5 g) as the reduction agent. CA confers the removal of O atoms from the [Bi2O2](2+) layer during the solvothermal process, resulting in the formation of plenty of oxygen vacancies in the Bi2WO6-x crystal. As a result, NIR photoabsorption of Bi2WO6-x nanodots can be remarkably enhanced with the increase of the CA amount from 0 to 1.0 g. Under irradiation of a single-wavelength (808 nm, 1.0 W cm(-2)) NIR laser, black Bi2WO6-x-CA(1.0) nanodots can not only efficiently produce a sufficient amount of heat with a photothermal conversion efficiency of 45.1% for photothermal therapy, but also generate singlet oxygen (O-1(2)) for photodynamic therapy. Furthermore, due to the presence of heavy-metal (Bi and W) elements, Bi2WO6-x-CA(1.0) nanodots have high X-ray attenuation ability for CT imaging. After the Bi2WO6-x-CA(1.0) nanodot dispersion is injected into the tumor-bearing mice, the tumor can be imaged by using CT and an IR thermal camera. After irradiation with a single-wavelength (808 nm, 1.0 W cm(-2), 10 min) NIR laser, the tumor can be completely suppressed by the synergic photothermal and photodynamic effects of Bi2WO6-x-CA(1.0) nanodots, without recurrence and treatment-induced toxicity. Therefore, Bi2WO6-x nanodots have great potential as a novel all-in-one nanoagent for the imaging and phototherapy of tumors.