Microstructure, Mechanical, and Corrosion Properties of Cast Heat-Resistant Al–4Zn–4Mg–4Cu–Zr–Y(Er) Alloy

M. V. Glavatskikh,L. E. Gorlov,R. Yu. Barkov,M. G. Khomutov,A. V. Pozdniakov

DOI: https://doi.org/10.1007/s11015-024-01620-w

2024-03-12

Metallurgist

Abstract:In this study, we analyze the microstructure, phase composition, aging process, and a set of characteristics of the performance properties of new casting Al–4Zn–4Mg–4Cu–0.2Zr alloys doped with yttrium (Y) or erbium (Er). Doping with Y or Er has been shown to decrease hot brittleness, enhance corrosion resistance, and slightly decrease strength characteristics at up to 200° C. When alloyed with Y or Er, enhanced casting properties are ensured through an increase in the proportion of eutectics and modification of the grain structure. The Al 8 Cu 4 Y, (Al, Cu) 11 Y 3 , Al 8 Cu 4 Er, and Al 3 Er phases containing Y and Er after homogenization at 465° C retain the shape of branched crystals, resulting in alloys with low ductility at up to 200° C. In all the alloys, after stretching at 250°C, the elongation considerably increases, and the yield strength is approximately the same and lies in the range of 217–222 MPa. Alloying with Y or Er results in less softening with increasing test temperature and considerably higher corrosion resistance under electrochemical corrosion conditions.

metallurgy & metallurgical engineering