Integrating cationic metal-organic frameworks with ultrafiltration membrane for selective removal of perchlorate from Water

Ting Li,Yi Ren,Shu Zhai,Weiming Zhang,Wenbin Zhang,Ming Hua,Lu Lv,Bingcai Pan

DOI: https://doi.org/10.1016/j.jhazmat.2019.120961

IF: 13.6

2020-01-01

Journal of Hazardous Materials

Abstract:We design a novel cationic metal-organic framework hybrid ultrafiltration polyvinylidene fluoride membrane (PVA/Cu-iMOFs/PVDF-0.05) and report its unique capture of aqueous perchlorate (ClO4-) at ppm-level. This membrane outperformed traditional adsorption materials and exhibited a specific affinity toward ClO4- in the presence of various competing anions at greater levels (up to a concentration ratio of 20). In the batch experiment, the ClO4- removal ratio reached 99.6% over a wide pH range (3(similar to)10). Membrane filtration by using a 12.56 cm(2) PVA/Cu-iMOFs/PVDF-0.05 membrane could effectively treat 4.71 L of ClO4--contaminated water before breakthrough occurred, while maintaining a satisfactory permeability ((similar to)627.32 L/(m(2)/h/bar)) and antifouling property. The exhausted membrane could easily be regenerated in aminoethanesulfonic acid solution for repeated use with a negligible decrease in capacity. Moreover, the membrane showed excellent long-term stability in a cross-flow filtration process due to the amido bond between the Cu-iMOFs and membrane surface as well as the "protection" of polyvinyl alcohol. Selective and reversible ion-exchange between the sulfonic acid (R-SO3) ligands of Cu-iMOFs and tetrahedral oxo-anionic species was verified to be the pathway for ClO4- trapping. Thus, other problematic elements that also occur in tetrahedral form in water can be removed by this method.