Theoretical Strength and Rubber-Like Behaviour in Micro-Sized Pyrolytic Carbon

Xuan Zhang,Lei Zhong,Arturo Mateos,Akira Kudo,Andrey Vyatskikh,Huajian Gao,Julia R. Greer,Xiaoyan Li

DOI: https://doi.org/10.1038/s41565-019-0486-y

IF: 38.3

2019-01-01

Nature Nanotechnology

Abstract:The creation of materials with a combination of high strength, substantial deformability and ductility, large elastic limit and low density represents a long-standing challenge, because these properties are, in general, mutually exclusive. Using a combination of two-photon lithography and high-temperature pyrolysis, we have created micro-sized pyrolytic carbon with a tensile strength of 1.60 ± 0.55 GPa, a compressive strength approaching the theoretical limit of ~13.7 GPa, a substantial elastic limit of 20–30% and a low density of ~1.4 g cm −3 . This corresponds to a specific compressive strength of 9.79 GPa cm 3 g −1 , a value that surpasses that of nearly all existing structural materials. Pillars with diameters below 2.3 μm exhibit rubber-like behaviour and sustain a compressive strain of ~50% without catastrophic failure; larger ones exhibit brittle fracture at a strain of ~20%. Large-scale atomistic simulations reveal that this combination of beneficial mechanical properties is enabled by the local deformation of 1 nm curled graphene fragments within the pyrolytic carbon microstructure, the interactions among neighbouring fragments and the presence of covalent carbon–carbon bonds.