Improvement of Ageing Issue in Zn0.4Fe2.1Co2Mn1.5O8 Thermistor Films

Wei Ren,Nan-Nan Zhu,Lu Li,Hong-Jian Feng,Yong-Gang Wang,Yan-Han Yang,Zhao-Ning Yang,Shi-Guang Shang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.05.068

IF: 5.7

2019-01-01

Journal of the European Ceramic Society

Abstract:The Zn-Fe-Mn-Co-O spinel-structured thermistor films were synthesized by chemical solution deposition methods. The ageing performance of these films was investigated by co-doping Fe and Zn into the films and annealing at different temperatures. The surface morphology and microstructure of these films were improved with the increasing temperature. The contents of Mn3+ and Mn4+ were stable with the annealing temperature due to iron and zinc co-doping. Annealing at 700 degrees C was necessary for the iron cation to be fully activated in the spinel lattice. The optimal electrical properties and ageing performance of the films were obtained at 800 degrees C, with an optimal B value of (similar to)4472 K and the lowest rate of change for the film resistance.