Metal-organic Composite Membrane with Sub-2 Nm Pores Fabricated Via Interfacial Coordination

Yu-Jie Shen,Li-Feng Fang,Yan,Jia-Jia Yuan,Zhi-Qiang Gan,Xiu-Zhen Wei,Bao-Ku Zhu

DOI: https://doi.org/10.1016/j.memsci.2019.05.070

IF: 9.5

2019-01-01

Journal of Membrane Science

Abstract:A metal-organic composite membrane with sub-2 nm pores was developed via interfacial coordination reaction in biphasic systems for the first time. Herein, tannic acid (TA) was dissolved in water, as aqueous phase; iron(III) acetylacetonate (Fe(acac)(3)), used as Fe(III) source, was dissolved in n-hexane as organic phase. A detailed study was conducted to obtain the defect-free TA-Fe(III) separation layer, including the salt concentration in aqueous solution, pH of the aqueous solution and the ratio of TA to Fe(acac)(3). The results indicated that the defect-free TA-Fe(III) composite membrane formed when the tris-complex (TA(3)-Fe(III)) was achieved. The optimal condition for preparing TA-Fe(III) composite membrane was using aqueous solution containing 0.4 M NaCl at pH=6 with the ratio of TA to Fe(acac)(3) of 10. Different from the typical separation layer formed on the membrane surface by interfacial polymerization, the TA-Fe(III) separation layer was formed in the pores of the substrate, which is attributed to the higher diffusion coefficient of Fe(acac)(3) from organic phase to aqueous phase. This work provided a novel strategy to fabricate metal-organic composite membrane with sub-2 nm pores; meanwhile, the new-prepared membrane shows a high Na2SO4 rejection of 97.3% with the water permeance of 8.6 Lm(-2) h(-1) bar(-1), and a high VB12 rejection of 97.6%, indicating an excellent ion/molecule separation performance.