Hierarchical Highly Wrinkled Trimetallic NiFeCu Phosphide Nanosheets on Nanodendrite Ni 3 S 2 /Ni Foam as an Efficient Electrocatalyst for the Oxygen Evolution Reaction
Meysam Khodabakhshi,Shumin Chen,Tian Ye,Hao Wu,Li Yang,Wenfeng Zhang,Haixin Chang
DOI: https://doi.org/10.1021/acsami.0c11732
2020-07-15
Abstract:The sluggish oxygen evolution reaction (OER) and costly noble-metal oxide catalysts hinder the vast usage of environmentally friendly water splitting for hydrogen production. Elemental doping by partial replacing of parent metal elements with elements of higher electronegativity is considered to be one of the most efficient strategies to promote the electrocatalytic OER performance. In this work, we synthesize an efficient hierarchical highly wrinkled NiFeCu phosphide nanosheet on nanodendrite Ni<sub>3</sub>S<sub>2</sub>/NiF substrates through partial replacement of Cu instead of Ni and Fe in <sub>3</sub>S<sub>2</sub>/NiF by using a facile electrodeposition method. The <sub>3</sub>S<sub>2</sub>/NiF electrocatalyst needs only 230, 282, and 351 mV to reach 10, 50, and 100 mA × cm<sup>–2</sup>, respectively. Notably, this electrocatalyst shows one of the lowest OER overpotentials at 10 mA/cm<sup>–2</sup> for metal phosphides and endured the OER at 20 mA × cm<sup>–2</sup> for 18 h with negligible voltage elevation. The X-ray photoelectron spectroscopy (XPS), double-layer capacitance (<i>C</i><sub>dl</sub>) plots, and electrochemical impedance spectroscopy show that the partial Cu doping in <sub>3</sub>S<sub>2</sub>/NiF not only can change the electron density around Ni and Fe but also can increase the electrochemically active surface area and conductivity of electrocatalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11732?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11732</a>.Optical images of untreated NiF and Ni<sub>3</sub>S<sub>2</sub>/NiF; SEM images of untreated Ni Foam; dense nanodendrite Ni<sub>3</sub>S<sub>2</sub> formed at the edge of Ni Foam and <sub>3</sub>S<sub>2</sub>/NiF; TEM images of <sub>3</sub>S<sub>2</sub>/NiF; EDX profile and wide XPS spectroscopy of <sub>3</sub>S<sub>2</sub>/NiF; electrochemical capacitance measurements of the relative ECSA of <sub>3</sub>S<sub>2</sub>/NiF and <sub>3</sub>S<sub>2</sub>/NiF; BET isotherm linear plot and corresponding Barrett–Joyner–Halenda (BJH) pore size distributions from the desorption branch of the isotherms for Ni<sub>3</sub>S<sub>2</sub>/NiF, <sub>3</sub>S<sub>2</sub>/NiF, and <sub>3</sub>S<sub>2</sub>/NiF; precursor concentration in 50 of mL Di-water electrodeposition solution; concentration of Ni–Fe–Cu and P elements for <sub>3</sub>S<sub>2</sub>/NiF and <sub>3</sub>S<sub>2</sub>/NiF electrocatalysts from XPS results; and BET isotherm linear results of Ni<sub>3</sub>S<sub>2</sub>/NiF, <sub>3</sub>S<sub>2</sub>/NiF, and <sub>3</sub>S<sub>2</sub>/NiF (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11732/suppl_file/am0c11732_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology