Degradation behaviors of Mg alloy wires/PLA composite in the consistent and staged dynamic environments

Xuan Li,Weidong Yu,Linyuan Han,Chenglin Chu,Jing Bai,Feng Xue

DOI: https://doi.org/10.1016/j.msec.2019.109765

2019-01-01

Abstract:Fully degradable poly lactic acid based composite reinforced with 20 vol% magnesium alloy wires (MAWs) is prepared for weight bearing bone fracture healing.

What problem does this paper attempt to address?

Fully Degradable PLA-based Composite Reinforced with 2D-Braided Mg Wires for Orthopedic Implants

Xuan Li,Chenglin Chu,Li Zhou,Jing Bai,Chao Guo,Feng Xue,Pinghua Lin,Paul K. Chu

DOI: https://doi.org/10.1016/j.compscitech.2017.02.013

IF: 9.1

2017-01-01

Composites Science and Technology

Abstract:Fully degradable poly-lactic acid (PLA) is reinforced with 2D-braided magnesium alloy wires (Mg wires or MAWs) for bone fixation devices. The relationship between the mechanical/degradation properties of the composite and microstructural features such as braiding angle, volume fraction, and interface properties is investigated. The biaxial mechanical properties of the composite can be tailored by the microstructure. When the braiding angle is 45°, the composite has the highest shear and impact strength and increasing the volume fraction simultaneously improves the tensile, bending, shear, and impact strength. Results obtained by the finite element method show that the screw hole undermines the safety factor of the composite under micro-strain. Acidic degradation of pure PLA can be mitigated by the corporation of MAWs and a degradation model is proposed to predict the mechanical properties of the composite during immersion. Our results reveal a relationship between the bending strength, molecular weight, and immersion time.
Biodegradable Poly-Lactic Acid Based-Composite Reinforced Unidirectionally with High-Strength Magnesium Alloy Wires.

X. Li,C.L. Chu,L. Liu,X.K. Liu,J. Bai,C. Guo,F. Xue,P.H. Lin,Paul K. Chu

DOI: https://doi.org/10.1016/j.biomaterials.2015.01.060

IF: 14

2015-01-01

Biomaterials

Abstract:Biodegradable poly-lactic acid (PLA) – based composites reinforced unidirectionally with high-strength magnesium alloy wires (MAWs) are fabricated by a heat-compressing process and the mechanical properties and degradation behavior are studied experimentally and theoretically. The composites possess improved strengthening and toughening properties. The bending strength and impact strength of the composites with 40 vol% MAWs are 190 MPa and 150 kJ/m2, respectively, although PLA has a low viscosity and an average molecular weight of 60,000 g/mol. The mechanical properties of the composites can be further improved by internal structure modification and interface strengthening and a numerical model incorporating the equivalent section method (ESM) is proposed for the bending strength. Micro arc oxidization (MAO) of the MAWs is an effective interfacial strengthening method. The composites exhibit high strength retention during degradation and the PLA in the composite shows a smaller degradation rate than pure PLA. The novel biodegradable composites have large potential in bone fracture fixation under load-bearing conditions.
Degradation Behaviors of PLA-matrix Composite with 20 Vol% Magnesium Alloy Wires under Static Loading Conditions

Chenglin Chu,Xuan Li,Weidong Yu,Linyuan Han,Jing Bai,Feng Xue

DOI: https://doi.org/10.1007/s10853-018-03199-5

IF: 4.5

2018-01-01

Journal of Materials Science

Abstract:Influence of static compression loading on the degradation behaviors of polylactic acid-based composite reinforced with 20 vol% magnesium alloy wires (MAWs) is investigated. The external stress would enhance the degradation of the composite. As the applied stress is increased from 1 to 3 MPa, the overall degradation rate goes up. After immersion for 30 days, the degradation rate of PLA matrix in the composite at the stress level of 3 MPa is about 1.46 and 2.4 times those at 1 and 0 MPa (unloading condition) while the bending strength retention is 0.73 and 0.63 times those of the latter ones. The relationship between the degradation rate of PLA matrix in the composite and the external compression stress is further elucidated. The external stress deteriorates the strength retention of the composite but a high MAWs content could mitigate the deterioration.
A study on Mg wires/poly-lactic acid composite degradation under dynamic compression and bending load for implant applications.

Xuan Li,Yu Wang,Chenglin Chu,Linyuan Han,Jing Bai,Feng Xue

DOI: https://doi.org/10.1016/j.jmbbm.2020.103707

IF: 4.042

2020-01-01

Journal of the Mechanical Behavior of Biomedical Materials

Abstract:A novel and economic device is developed for simulating the physiological mechanochemical conditions. The degradation behaviors of poly-lactic acid (PLA) based composite reinforced with magnesium alloy wires (Mg wires/PLA) under dynamic compression and bending loads are investigated. The results denote the dynamic loads significantly influence the degradation behaviors of the composite. The dynamic bending load would profoundly promote the degradation of Mg wires in the composite and then accelerate the mechanical properties loss of the composite. The bending strength retention of the composite under consistent dynamic bending load at a magnitude of 5.6 N (about 5.6 MPa for the maximum stress at the middle surface) after 21 days immersion is about 53.3%, comparing to 69.7% for the dynamic compression load at a magnitude of 12 N (0.5 MPa for the compression stress). Furthermore, a numerical model is successfully postulated to elucidate the bending strength evolution of the composite under different dynamic loading conditions.
Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

SHEN Lie,QIAO Fei,ZHANG Yuqiang,ZHANG Zhiyan,PENG Mao,ZHU Feiyan

DOI: https://doi.org/10.3321/j.issn:1000-3851.2007.05.012

2007-01-01

Abstract:A novel composite of carbon fiber(CF) reinforced hydroxyapatite(HA)/ploylactide(PLA) degradable biomaterial was developed by solvent blending.The mechanical properties and degradation properties in vitro of the composite were researched.The CF/HA/PLA composites have excellent mechanical properties.As the hydroxyapatite mass fraction increases,there are respectively peak values with flexural strength and flexural modulus,including maximums of flexural strength of 430MPa and flexural modulus of 26GPa.After degradating in vitro for 3 months,the flexural strength and flexural modulus fall 30% and 36% respectively.The SEM photos indicate that the degradation begins from the interfaces of the composite,after degradating,there are gaps at the interfaces,and the water uptake increases to 5%,but the mass loss is only 1.6%.The pH values of the PBS drop less than 0.1,which can do some favors to the recoveries of the fracture.The results show that the mechanical properties of the composite can meet the requirements of internal fracture fixation.
In Vitro Degradation Behavior of Mg Wire/poly(lactic Acid) Composite Rods Prepared by Hot Pressing and Hot Drawing.

Hong Cai,Jiao Meng,Xuan Li,Feng Xue,Chenglin Chu,Chao Guo,Jing Bai

DOI: https://doi.org/10.1016/j.actbio.2019.05.059

IF: 10.633

2019-01-01

Acta Biomaterialia

Abstract:In this study, we prepared Mg wire/poly(lactic acid) composite rods by hot pressing (HP) and hot drawing (HD) processes, which show desirable application potential as a biodegradable implant in orthopedics. The influences of the volume content of Mg wires and processing steps on the degradation behavior of composite rods as well as the mutual influence between Mg and poly(lactic acid) (PLA) during degradation were investigated. During degradation, the improved interface bonding between Mg and PLA by micro-arc oxidation can effectively inhibit the diffusion of the medium from the ends to the central part, supported by XR-CT results, which show the degradation cracks in PLA initiated and propagated along the radial direction of the rod rather than the axial direction. When compared with the hot pressed rod, the three passes hot drawn rod had lower degradation rate and better strength retention during long-time immersion. This is ascribed to the higher crystallinity of the PLA matrix by HD. For both hot pressed and hot drawn rods, more Mg content of the wires will result in an increase in the degradation rate of PLA due to alkaline catalytic hydrolysis. Therefore, we can not only predict the degradation period by the present degradation mathematical model but also further control degradation rate by adjusting processing steps and wire volume content. This will be helpful for future material design and indication selection. STATEMENT OF SIGNIFICANCE: We investigated the influence of interface microstructure, self-reinforced PLA matrix, and wire volume content on the degradation behavior and clarified the differences in the degradation mechanism of composite rods. The 3D morphology of cracks in composite rods enlightened us a clear understanding about the emergence and evolution of cracks, which revealed the reason for the failure of composite rods. The degradation model can be used to predict the degradation period and provide valuable information for their future application.
Internal Morphology Evolution of Mg Wire/Poly(Lactic Acid) Composites During Degradation Process Characterized by X-Ray Computed Tomography

Cai Hong,Xue Feng,Chu Chenglin,Bai Jing,Wang Hongxing,Zhu Ding,Li Xuan,Han Bing,Gao Wentong,Hang Zusheng

DOI: https://doi.org/10.1007/s11665-021-06555-w

IF: 2.3

2022-01-01

Journal of Materials Engineering and Performance

Abstract:The composite rod composed of magnesium alloy wire and poly(lactic acid) (Mg wire/PLA) was prepared by hot-pressed process. The internal morphology evolution of the composites during degradation was investigated by x-ray computed tomography (XCT). Particularly, the location, amount, size, as well as sphericity of defects were visualized on the basis of XCT three-dimensional imaging technology and VGDefX algorithm. The result denoted that cracks were prone to appear near the outside location of the composites. The diameter-sphericity and volume-sphericity of defects inside the composites significantly increased after 6 weeks immersion. The alkaline degradation products in composite rods induced by the degradation of magnesium would promote the degradation of PLA and further accelerate the mechanical properties loss. Reasons for the inhomogeneity of degradation morphology were analyzed from the view of Mg wire, PLA matrix, as well as interface bonding state. Furthermore, the relationship between the evolution of degradation morphology and the attenuation of mechanical properties of the composites was presented. It is of great significance to provide theoretical guidance and method reference for in situ investigating the degradation performances of this kind of composites.
Mg alloy rod reinforced biodegradable poly-lactic acid composite for load bearing bone replacement

Muhammad Shoaib Butt,Jing Bai,Xiaofeng Wan,Chenglin Chu,Feng Xue,Hongyan Ding,Guanghong Zhou

DOI: https://doi.org/10.1016/j.surfcoat.2016.12.005

IF: 4.865

2017-01-01

Surface and Coatings Technology

Abstract:Absorbable medicinal devices must be fabricated in order to have a suitable degradation rate in agreement with the healing rate of bone in the implantation site. In this work one of the naturally biodegradable poly-lactic acids composite reinforced with (AZ31) magnesium alloy rod for potential application and there in-vitro degradation is investigated during 8weeks. There microstructures, mechanical properties, immersion corrosion and surface/interface behavior were studied. Fluoride conversion coatings formed porous MgF2 ceramic layer on Mg rod surface. The results show that the Mg rod reinforced poly-lactic acid plays a crucial role in the degradation rate of PLA/Mg composite, treated with hydrofluoric acid promoting a lower degradation rate than untreated sample. This fact is only due to micro-anchoring effect, leading to better mechanical properties and degradation performance in simulated body fluid solution. Untreated promote a faster formation of cracks and, therefore, an increasingly faster degradation of the polymeric matrix. With prolonging immersion time until 8weeks, the MgF2 porous coatings were corroded gradually, along with the disappearance of original pores and the formation of a relatively smooth surface. It resulted in a rapid reduction in mechanical properties for corresponding composite rods owing to the weakening of interfacial binding capacity between poly-lactic acid and inner layer. The present results indicated that this new Mg alloy rod reinforced poly-lactic acid composite rods show a potential for biomedical applications.
Influence of Dynamic Compressive Loading on the in Vitro Degradation Behavior of Pure PLA and Mg/PLA Composite.

Xuan Li,Chenxi Qi,Linyuan Han,Chenglin Chu,Jing Bai,Chao Guo,Feng Xue,Baolong Shen,Paul K Chu

DOI: https://doi.org/10.1016/j.actbio.2017.08.004

IF: 10.633

2017-01-01

Acta Biomaterialia

Abstract:The effects of dynamic compressive loading on the in vitro degradation behavior of pure poly-lactic acid (PLA) and PLA-based composite unidirectionally reinforced with micro-arc oxidized magnesium alloy wires (Mg/PLA) are investigated. Dynamic compressive loading is shown to accelerate degradation of pure PLA and Mg/PLA. As the applied stress is increased from 0.1MPa to 0.9MPa or frequency from 0.5Hz to 2.5Hz, the overall degradation rate goes up. After immersion for 21days at 0.9MPa and 2.5Hz, the bending strength retention of the composite and pure PLA is 60.1% and 50%, respectively. Dynamic loading enhances diffusion of small acidic molecules resulting in significant pH decrease in the immersion solution. The synergistic reaction between magnesium alloy wires and PLA in the composite is further clarified by electrochemical tests. The degradation behavior of the pure PLA and PLA matrix in the composite under dynamic conditions obey the first order degradation kinetics and a numerical model is postulated to elucidate the relationship of the bending strength, stress, frequency, and immersion time under dynamic conditions.STATEMENT OF SIGNIFICANCE:We systematically study the influence of dynamic loading on the degradation behavior of pure PLA and Mg/PLA. Dynamic compressive loading is shown to accelerate degradation of pure PLA and Mg/PLA. The synergistic reaction between magnesium alloy wires and PLA in the composite is firstly clarified by electrochemical tests. The degradation behavior of the pure PLA and PLA matrix in the composite under dynamic conditions obey the first order degradation kinetics. Then, a numerical model is postulated to elucidate the relationship of the bending strength, stress, frequency, and immersion time under dynamic conditions.
Degradation Behaviors of Surface Modified Magnesium Alloy Wires in Different Simulated Physiological Environments

Xuan Li,Chao Shi,Jing Bai,Chao Guo,Feng Xue,Ping-Hua Lin,Cheng-Lin Chu

DOI: https://doi.org/10.1007/s11706-014-0257-5

2014-01-01

Abstract:The degradation behaviors of the novel high-strength AZ31B magnesium alloy wires after surface modification using micro-arc-oxidization (MAO) and subsequently sealing with poly-L-lactic acid (PLLA) in different simulated physiological environments were investigated. The results show the surface MAO micropores could be physically sealed by PLLA, thus forming an effective protection to corrosion resistance for the wires. In simulated gastric fluid (SGF) at a low pH value (1.5 or 2.5), the treated wires have a high degradation rate with a rapid decrease of mass, diameter, mechanical properties and a significant increase of pH value of the immersion fluid. However, surface modification could effectively reduce the degradation rate of the treated wires in SGF with a pH value above 4.0. For the treated wires in simulated intestinal fluid at pH = 8.5, their strength retention ability is higher than that in strong acidic SGF. And the loss rate of mass is faster than that of diameter, while the pH value of the immersion fluid decreases. It should be noted that the modified wires in simulated body environment have the best strength retention ability. The wires show the different degradation behaviors indicating their different degradation mechanisms, which are also proposed in this work.
Impact Behaviors of Poly-Lactic Acid Based Biocomposite Reinforced with Unidirectional High-Strength Magnesium Alloy Wires

Xuan Li,Chao Guo,Xiaokai Liu,Lei Liu,Jing Bai,Feng Xue,Pinghua Lin,Chenglin Chu

DOI: https://doi.org/10.1016/j.pnsc.2014.08.003

2014-01-01

Abstract:A novel poly-lactic acid（PLA） based biocomposite reinforced with unidirectional high-strength magnesium alloy（Mg-alloy） wires for bone fracture fixation was fabricated by hot-compressing process. The macroscopical and microscopical impact behaviors of the biocomposite were investigated using impact experiments and finite element method（FEM）, respectively. The results indicated that the biocomposite had favorable impact properties due to the plastic deformation behavior of Mg-alloy wires during impact process. While the content of Mg-alloy wires reached20 vol%, the impact strength of the composite could achieve 93.4 k J/m2, which is approximate 16 times larger than that of pure PLA fabricated by the same process. According to FEM simulation results, the complete destruction life of the composites during impact process increased with increasing volume fraction of Mg-alloy wires, indicating a high impact-bearing ability of the composite for bone fracture fixation.Simultaneously, the energy absorbed by Mg-alloy wires in the composites had a corresponding increase. In addition, it denoted that the impact properties of the composites are sensitive to the initial properties of the matrix material.
Enhanced Fully-Biodegradable Mg/PLA Composite Rod: Effect of Surface Modification of Mg-2Zn Wire on the Interfacial Bonding

Hong Cai,Yue Zhang,Jiao Meng,Xuan Li,Feng Xue,Chenglin Chu,Li Tao,Jing Bai

DOI: https://doi.org/10.1016/j.surfcoat.2018.07.045

2018-01-01

Abstract:The fully-biodegradable composite rod with Mg-2Zn wires reinforced polylactic acid (PLA) for potential application in orthopedic internal fixation was prepared by hot-press method in this work. We performed different surface modifications on Mg-2Zn wires including micro-arc oxidation (MAO) and chemical conversion using dopamine (DA), hydrogen fluoride acid (HF) and gamma-aminopropyltriethoxysilane (KH550). In contrast, MAO treatment significantly improved the interfacial bonding between wires and PLA matrix due to the strong electrostatic interaction and the micro-anchoring interaction according to single wire pull-out experiments and molecular dynamic simulation. The surface roughness of wires after MAO is 192.0 +/- 5.0 nm, most of pore size are in the range of 0.5-1.5 mu m and the average interface thickness is about 1.5 mu m. The essential reason leading to the differences of interfacial bonding is revealed from atomic level, which is useful for optimizing the preparation technology of Mg-2Zn wires/PLA composite rod.
Self-reinforced Biodegradable Mg-2Zn Alloy Wires/polylactic Acid Composite for Orthopedic Implants

Hong Cai,Yue Zhang,Xuan Li,Jiao Meng,Feng Xue,Chenglin Chu,Li Tao,Jing Bai

DOI: https://doi.org/10.1016/j.compscitech.2018.04.040

IF: 9.1

2018-01-01

Composites Science and Technology

Abstract:Biodegradable composite rods with polylactic acid as matrix and Mg-2Zn wires as the reinforcement body were prepared by hot press and hot drawn method in this article. The main purpose is to improve the mechanical properties based on the strengthen and toughness effect of the directionally distributed Mg-2Zn wires in PLA matrix and the improved interfacial bonding strength by MAO treated Mg-2Zn wires as well as the self-reinforcement effect of PLA after hot drawn process. The effect of hot drawn on the orientation, crystallinity and melting temperature changes of PLA were investigated by XRD and DSC method. The relationship between the bending strength and the volume content of Mg-2Zn wires in the composite rods as well as the influence of hot drawn on the mechanical properties were compared and analyzed theoretically. The regularly arrangement of PLA chains after hot drawn is benefit to increase the crystallinity, the elastic modulus as well as the mechanical strength in essence. Theoretical calculation results could provide a reference value and guide us to adjust the Mg-2Zn wires content and prepare the composite rods according to the actual application requirements.
Selective Laser Sintering PLA/Mg Composite Scaffold with Promoted Degradation and Enhanced Mechanical

Li, Dongying

DOI: https://doi.org/10.1007/s10924-024-03208-6

IF: 4.705

2024-03-26

Journal of Polymers and the Environment

Abstract:Polylactic acid (PLA) is widely used in the treatment of bone defects due to its good properties, but the problem of its slow degradation rate needs to be solved urgently. In this study, different proportions of Mg were introduced into PLA to promote and regulate its degradation. A three-dimensional porous composite bone scaffold made of PLA and Mg was prepared using selective laser sintering (SLS). Degradation results showed that the weight loss rate of the Mg-containing scaffold within 4 weeks was nearly five times higher than that of the pure PLA scaffold. Moreover, the degradation mechanism was further explored, and it was believed that the addition of Mg could consume the acidic degradation products of PLA, thus destroying the integrity of the PLA molecular chain and accelerating the flow of the molecular chain, ultimately forming a cycle that promotes degradation. In addition, the magnesium-containing scaffold (PLA/3Mg) also showed good compressive strength (5.6 MPa), which was nearly twice as high as that of the pure PLA scaffold (2.67 MPa). Therefore, we believe that introducing an appropriate amount of Mg can better adjust the balance between the degradation and mechanical properties of PLA scaffolds.

engineering, environmental,polymer science
Additively-manufactured Mg wire-reinforced PLDL-matrix composites for biomedical applications

C. Thompson,C. González,J. LLorca

DOI: https://doi.org/10.1016/j.jmbbm.2024.106496

IF: 4.042

2024-03-04

Journal of the Mechanical Behavior of Biomedical Materials

Abstract:Coupons of a medical grade PLDL polymer matrix uniaxially reinforced with a 15% volume fraction of Mg wires have been manufactured by fused deposition modelling for the first time. Two different types of Mg wires, without and with a surface treatment by plasma electrolytic oxidation were used. Both composite materials were subjected to degradation in phosphate buffer solution over a 3-week period, and their degradation and deformation micromechanisms were analysed in detail. Additionally, the materials were subjected to extensive mechanical testing under various loading conditions, and the interface strength was also analysed. It was found that the presence of the Mg wires improves the mechanical behavior and accelerates the corrosion rate of the composite with respect that of the polymer matrix and these properties can be further tailored through the surface-modification of Mg wires by plasma electrolytic oxidation. The additive manufacturing strategy presented opens the path to fabricate multimaterial implants and scaffolds with complex shape and tailored properties provided by biodegradable polymers reinforced with either Mg and Zn particles and/or wires.

engineering, biomedical,materials science, biomaterials
A Study on the Impact Behaviors of Mg Wires/pla Composite for Orthopedic Implants

Xuan Li,Linyuan Han,Xiaokai Liu,Chenglin Chu,Jia Ju,Jing Bai,Xiaobo Zhang

DOI: https://doi.org/10.1007/s10853-019-03955-1

IF: 4.5

2019-01-01

Journal of Materials Science

Abstract:Polylactic acid (PLA)-based composite reinforced with magnesium alloy wires (Mg wires) is prepared by lamina stack method for orthopedic implants. The impact behaviors of the composite are experimentally and theoretically studied. The results suggest that Mg wires could significantly improve the impact performances of PLA. The initial impact strength of the composite with 10 vol% Mg wires is about 5 times that of pure PLA. After 3 weeks, immersion at 50 °C, the impact strength of the composite at 10 vol% could retain to be 10 kJ/m2, while pure PLA losses its impact strength. Further theoretical studies by finite element method indicate a small diameter for the wires could significantly improve the impact properties of the composite and promote the energy absorption of the wire components. Moreover, increasing the lamina numbers could also improve the impact properties of the composite.
Long-term and uniform release of magnesium ions from PLA porous composite materials oriently reinforced by Mg wires for potential bone repair application

Shanyun Sun,Lei Gao,Bin Liang,Zhaowei Yin,Shaowei Pan,Chen Shi,Chao Guo,Zhihai Huang,Chenglin Chu,Yinsheng Dong

DOI: https://doi.org/10.1016/j.surfin.2023.103018

IF: 6.2

2023-06-28

Surfaces and Interfaces

Abstract:PLA based porous composite materials oriently reinforced by ordinary Mg wires (PLA-Mg) and biomimetic-treated Mg wires (PLA-MC) were fabricated. PLA-Mg and PLA-MC both realized long-term and uniform release of Mg 2+ . Compared by PLA-Mg, the release of Mg 2+ of PLA-MC was more uniform. The presence of Mg wires promoted the hydrolysis of PLA in PLA-Mg, which featured with crystallinity of PLA in immersed PLA-Mg reaching 0.67 with an increase of 19.6% compared with immersed PLA. Comparatively, the degradation of PLA in PLA-MC was lower and regulated, which was characterized by crystallinity reaching 0.55 with a decrease of 1.8% compared with soaked PLA. Moreover, the release of Mg 2+ in PLA-Mg and PLA-MC both followed exponential rules of decline, which could be used for predicting that the final C(Mg 2+ ) approached 41.67 and 40.83 ppm by mathematical models, respectively. More obvious cell adhesion and cell viability at interface between PLA oriented pore walls and biomimetic-treated Mg wire endowed PLA-MC with better biocompatibility than PLA-Mg or PLA, exhibiting the greatest capacity of cell adhesion and proliferation due to more stable variation in pH and the long-term smaller release of Mg 2+ . The results could provide references for the development of new bone repair materials.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
Biodegradable Mg Strengthened Poly-Lactic Acid Composite Through Interfacial Properties

Muhammad Shoaib Butt,Jing Bai,Xiaofeng Wan,Chenglin Chu,Feng Xue,Hongyan Ding,Guanghong Zhou

DOI: https://doi.org/10.4028/www.scientific.net/msf.900.7

2017-01-01

Materials Science Forum

Abstract:High-strength magnesium alloy (AZ31) reinforced poly-lactic acid (PLA) composite rods for potential application of bone fracture fixation prepared by plastic injection process on Mg rod.Thecomposities possess improved the interfacial bonding between poly-lactic acid and Mg rod due to the micro-anchoring which lead to better mechanical performance in Simulated body fluid solution.The present results indicated that this new PLA-clad Mg composite rods show good potential for biomedical applications.
Preparation, microstructure and degradation performance of biomedical magnesium alloy fine wires

jing bai,l yin,ye lu,yiwei gan,feng xue,chenglin chu,jingli yan,kai yan,xiaofeng wan,zhejun tang

DOI: https://doi.org/10.1016/j.pnsc.2014.08.015

2014-01-01

Abstract:With the development of new biodegradable Mg alloy implant devices, the potential applications of biomedical Mg alloy fine wires are realized and explored gradually. In this study, we prepared three kinds of Mg alloy fine wires containing 4wt% RE(Gd/Y/Nd) and 0.4wt% Zn with the diameter less than 0.4μm through casting, hot extruding and multi-pass cold drawing combined with intermediated annealing process. Their microstructures, mechanical and degradation properties were investigated. In comparison with the corresponding as-extruded alloy, the final fine wire has significantly refined grain with an average size of 3–4μm, and meanwhile shows higher yield strength but lower ductility at room temperature. The degradation tests results and surface morphologies observations indicate that Mg–4Gd–0.4Zn and Mg–4Nd–0.4Zn fine wires have similar good corrosion resistance and the uniform corrosion behavior in SBF solution. By contrast, Mg–4Y–0.4Zn fine wire shows a poor corrosion resistance and the pitting corrosion behavior.
In Vitro Degradation of MAO/PLA Coating on Mg-1.21Li-1.12Ca-1.0Y Alloy

Rong-Chang Zeng,Wei-Chen Qi,Ying-Wei Song,Qin-Kun He,Hong-Zhi Cui,En-Hou Han

DOI: https://doi.org/10.1007/s11706-014-0264-6

2014-01-01

Frontiers of Materials Science

Abstract:Magnesium and its alloys are promising biomaterials due to their biocompatibility and osteoinduction. The plasticity and corrosion resistance of commercial magnesium alloys cannot meet the requirements for degradable biomaterials completely at present. Particularly, the alkalinity in the microenvironment surrounding the implants, resulting from the degradation, arouses a major concern. Micro-arc oxidation (MAO) and poly(lactic acid) (PLA) composite (MAO/PLA) coating on biomedical Mg--1.21Li--1.12Ca--1.0Y alloy was prepared to manipulate the pH variation in an appropriate range. Surface morphologies were discerned using SEM and EMPA. And corrosion resistance was evaluated via electrochemical polarization and impedance and hydrogen volumetric method. The results demonstrated that the MAO coating predominantly consisted of MgO, Mg2SiO4 and Y2O3. The composite coating markedly improved the corrosion resistance of the alloy. The rise in solution pH for the MAO/PLA coating was tailored to a favorable range of 7.5--7.8. The neutralization caused by the alkalinity of MAO and Mg substrate and acidification of PLA was probed. The result designates that MAO/PLA composite coating on Mg--1.21Li--1.12Ca--1.0Y alloys may be a promising biomedical coating.

Degradation behaviors of Mg alloy wires/PLA composite in the consistent and staged dynamic environments

Fully Degradable PLA-based Composite Reinforced with 2D-Braided Mg Wires for Orthopedic Implants

Biodegradable Poly-Lactic Acid Based-Composite Reinforced Unidirectionally with High-Strength Magnesium Alloy Wires.

Degradation Behaviors of PLA-matrix Composite with 20 Vol% Magnesium Alloy Wires under Static Loading Conditions

A study on Mg wires/poly-lactic acid composite degradation under dynamic compression and bending load for implant applications.

Mechanical Properties and Degradation Properties in Vitro of Carbon Fiber Reinforced Hydroxyapatite/polylactide Composite

In Vitro Degradation Behavior of Mg Wire/poly(lactic Acid) Composite Rods Prepared by Hot Pressing and Hot Drawing.

Internal Morphology Evolution of Mg Wire/Poly(Lactic Acid) Composites During Degradation Process Characterized by X-Ray Computed Tomography

Mg alloy rod reinforced biodegradable poly-lactic acid composite for load bearing bone replacement

Influence of Dynamic Compressive Loading on the in Vitro Degradation Behavior of Pure PLA and Mg/PLA Composite.

Degradation Behaviors of Surface Modified Magnesium Alloy Wires in Different Simulated Physiological Environments

Impact Behaviors of Poly-Lactic Acid Based Biocomposite Reinforced with Unidirectional High-Strength Magnesium Alloy Wires

Enhanced Fully-Biodegradable Mg/PLA Composite Rod: Effect of Surface Modification of Mg-2Zn Wire on the Interfacial Bonding

Self-reinforced Biodegradable Mg-2Zn Alloy Wires/polylactic Acid Composite for Orthopedic Implants

Selective Laser Sintering PLA/Mg Composite Scaffold with Promoted Degradation and Enhanced Mechanical

Additively-manufactured Mg wire-reinforced PLDL-matrix composites for biomedical applications

A Study on the Impact Behaviors of Mg Wires/pla Composite for Orthopedic Implants

Long-term and uniform release of magnesium ions from PLA porous composite materials oriently reinforced by Mg wires for potential bone repair application

Biodegradable Mg Strengthened Poly-Lactic Acid Composite Through Interfacial Properties

Preparation, microstructure and degradation performance of biomedical magnesium alloy fine wires

In Vitro Degradation of MAO/PLA Coating on Mg-1.21Li-1.12Ca-1.0Y Alloy