Enhancing Red Upconversion Emission of Ho3+ Ions Through Constructing NaYF4:Yb3+/Ho3+/Ce3+@NaYF4:Yb3+/Nd3+core-shell Structures
Dong Jun,Zhang Chen-Xue,Cheng Xiao-Tong,Xing Yu,Han Qing-Yan,Yan Xue-Wen,Qi Jian-Xia,Liu Ji-Hong,Yang Yi,Gao Wei
DOI: https://doi.org/10.7498/aps.70.20210118
IF: 0.906
2021-01-01
Acta Physica Sinica
Abstract:The red upconversion (UC) emission of Ho3+ ions is located in an “optical window” range of the biological tissue, which has great prospects in the biology application. In this work, the NaYF4:20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:x%Yb3+ and NaYF4:20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:15%Yb3+/x%Nd3+ core-shell (CS) nanoparticles (NPs) are built based on the epitaxial growth technology by the high-temperature co-precipitation method in order to enhance red UC emission. The crystal structure and morphology of NaYF4 CS NPs are characterized by X-ray diffraction and transmission electron microscope. It can be found that the morphology of NaYF4 CS NPs changes from sphere into rod shape when coated with NaYF4 shell, and has a pure hexagonal-phase crystal structure. Under 980 nm excitation, the red UC emission intensity of NaYF4:20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:5%Yb3+ CS NPs is strongest and enhanced about 5.2 times than that of NaYF4:20%Yb3+/2%Ho3+/12%Ce3+ NPs. Under 800 nm excitation, the red emission intensity of NaYF4:20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:15%Yb3+/20%Nd3+ CS NPs is increased about 6.1 times compared with that of the NaYF4:20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:15%Yb3+/5%Nd3+ CS NPs. This is because the constructed CS effectively reduces the non-radiative decay from the surface defects of NPs, and the doped Yb3+ and Nd3+ ions in the NaYF4 shells can transfer more excitation energy to Ho3+ ions in the core. In addition, the NaYF4: 20%Yb3+/2%Ho3+/12%Ce3+@NaYF4:15%Yb3+/20%Nd3+ CS NP is excited by dual-wavelengths co-excitation (800 nm + 980 nm). It is found that the red UC emission intensity under the co-excitation of dual-wavelengths is higher than the sum of the excitation intensities of two single wavelengths (800 nm and 980 nm), which is due to the synergistic effect generated under the co-excitation of 980 nm and 800 nm near infrared laser. Therefore, different CS structures constructed by introducing different energy transfer channels can achieve the enhancement of the red UC emission under different excitation conditions, and the dual-wavelength co-excitation provides a new way to improve the penetration depth and the detection sensitivity for further expanding the applications in the field of biomedicine.