Abstract:The correlation between the accelerated corrosion and atmospheric corrosion is needed in order to study the degradation of mechanical properties, based on the former. To achieve that end, static tensile tests were performed on 78 specimens under three different environments: urban industrial atmospheric corrosion, dry/wet cyclic accelerated corrosion in a laboratory as simulated from the urban industrial atmosphere, and machinesimulated corrosion; and the effects of corrosion method and corrosion degree on the constitutive law of corroded steel plates were investigated based on the corrosion morphology. Moreover, the degree of correlation for the corrosion level assessment and mechanical properties indices were analyzed between the atmospheric corrosion and accelerated corrosion, based on the grey relational analysis. As a result, the mechanical properties decrease and the dispersion increases with the increasing corrosion degree. When the mass loss is >= 16%, the yield plateau of the stress-strain curve of corroded steel plate is significantly shortened. The mass loss of 30% can be defined as the critical point at which the yielding plateau disappears under the dry/wet cyclic accelerated corrosion test. The critical corrosion ratios for the main mechanical indices not meeting the specification requirements are proposed; and the relationship between the etch pit depth and mechanical property degradation is established along with a deterministic constitutive model related to the corrosion ratio. The degree of correlation for either the corrosion level assessment index or the mechanical property index is found to be good. The mechanical properties of corroded steel under the acid rain corrosion environment may be better simulated by the dry/wet cyclic accelerated corrosion or the machine-simulated corrosion when both pitting corrosion and uniform corrosion are considered.

Comparison on Corrosion Behaviour and Mechanical Properties of Structural Steel Exposed Between Urban Industrial Atmosphere and Laboratory Simulated Environment

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Corrosion Behaviors and Mechanical Properties of Q235 Steel Pipes Collapsing Due to Corrosion after 25-Year Service in Urban Industrial Atmospheric Environment

Comparison on Mechanisms of High-Cycle Fatigue Performance of Structural Steel Exposed to Urban Industrial Atmosphere and Laboratory Simulated Corrosive Environment Based on Infrared Thermography

Grey Relational Analysis of Static Tensile Properties of Structural Steel Subjected to Urban Industrial Atmospheric Corrosion and Accelerated Corrosion

Corrosion Behaviors and Mechanisms of New Weathering Steel and Carbon Steel in Simulated Industrial Atmosphere

High-Temperature Mechanical Properties of Artificially Simulated Corroded Q500MC Structural Steel

The Corrosion Resistance of Weathering Steels in Atmospheric Exposure and Laboratory-accelerated Corrosion Tests

Corrosion Behaviour and Mechanical Property Degradation of Q355b Steel under Coupled Environmental Loads

Study on Corrosion Models of Structural Steel Exposed in Urban Industrial Atmospheric and Laboratory Simulated Environments Based on the 3D Profile

Experimental and Theoretical Study on Mechanical Properties of Mild Steel after Corrosion

Experimental Study on Fatigue Crack Growth and Residual Strength of Steel 30crmnsini2a under Mixed Corrosive Environments

Corrosion behavior of high strength weathering steels in simulated industrial atmosphere environment

Corrosion Behavior and Mechanical Properties of 30crmnsia High-Strength Steel under an Indoor Accelerated Harsh Marine Atmospheric Environment

Mechanical Performance of Corroded Steel Bars in Concrete

EXPERIMENTAL STUDY ON THE DETERIORATION OF MECHANICAL PROPERTIES OF CORRODED STEEL

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Experimental and Numerical Analysis of Mechanical Behaviors of Long-Term Atmospheric Corroded Q235 Steel

Corrosion Behavior of New Weathering Steel in the Environment Simulating Coastal Industrial Atmosphere

Rust Layer of Steel Under Various Corrosion Environments

Corrosion behavior of weathering steel in marine atmosphere