Atomic Structure Evolution of Pt–Co Binary Catalysts: Single Metal Sites versus Intermetallic Nanocrystals
Xing Li,Yanghua He,Shaobo Cheng,Boyang Li,Yachao Zeng,Zhenhua Xie,Qingping Meng,Lu Ma,Kim Kisslinger,Xiao Tong,Sooyeon Hwang,Siyu Yao,Chenzhao Li,Zhi Qiao,Chongxin Shan,Yimei Zhu,Jian Xie,Guofeng Wang,Gang Wu,Dong Su
DOI: https://doi.org/10.1002/adma.202106371
IF: 29.4
2021-10-04
Advanced Materials
Abstract:Due to their exceptional catalytic properties for the oxygen reduction reaction (ORR) and other crucial electrochemical reactions, PtCo intermetallic nanoparticle (NP) and single atomic (SA) Pt metal site catalysts have received considerable attention. However, their formation mechanisms at the atomic level during high-temperature annealing processes remain elusive. Here, the thermally driven structure evolution of Pt–Co binary catalyst systems is investigated using advanced in situ electron microscopy, including PtCo intermetallic alloys and single Pt/Co metal sites. The pre-doping of CoN4 sites in carbon supports and the initial Pt NP sizes play essential roles in forming either Pt3Co intermetallics or single Pt/Co metal sites. Importantly, the initial Pt NP loadings against the carbon support are critical to whether alloying to L12-ordered Pt3Co NPs or atomizing to SA Pt sites at high temperatures. High Pt NP loadings (e.g., 20%) tend to lead to the formation of highly ordered Pt3Co intermetallic NPs with excellent activity and enhanced stability toward the ORR. In contrast, at a relatively low Pt loading (<6 wt%), the formation of single Pt sites in the form of PtC3N is thermodynamically favorable, in which a synergy between the PtC3N and the CoN4 sites could enhance the catalytic activity for the ORR, but showing insufficient stability.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology