Free-Standing Ultrafine Nanofiber Papers with High PM 0.3 Mechanical Filtration Efficiency by Scalable Blow and Electro-Blow Spinning
Yibo Liu,Chao Jia,Han Zhang,Haiyang Wang,Pan Li,Luna Jia,Feng Wang,Pengfei Zhu,Hao Wang,Lu Yu,Feipeng Wang,Lingxiao Wang,Xin Zhang,You Sun,Bo Li
DOI: https://doi.org/10.1021/acsami.1c04253
2021-07-19
Abstract:Particulate matter of 0.3 μm in diameter (PM<sub>0.3</sub>) poses a serious threat to the environment and human beings. Ultrathin and -light nanofibrous filters with excellent filtration properties can significantly prevent the detrimental effects of these particles. Here, we develop free-standing polyamide PA-66 ultrafine nanofiber papers for PM<sub>0.3</sub> filtration using effective and scalable blow and electro-blow spinning techniques. The smallest average fiber diameter is 61.7 nm, which is 2–3 orders of magnitude smaller than that of conventional textiles. Poly(ethylene terephthalate) nonwovens are selected to fabricate free-standing nanofiber papers of various polymers, including polyamide, poly(methyl methacrylate), poly(vinylpyrrolidone), and poly(ethylene oxide) owing to the smooth surfaces of the nonwovens. This underlying principle can be used to create similar free-standing nanofiber papers from other commodity polymers in the future. Mechanisms of capturing particulate matter with different nanofiber morphologies are discussed. Salt and oil particulates are used to characterize the filtration properties. PA-66 papers are promising reusable filters owing to their mechanical particle-capture mechanism. The blow-spun PA-66 papers show filtration performance of 98.75% efficiency and a pressure drop of 125.44 Pa owing to the "slip" effect caused by the ultrasmall diameter. In the electro-blow spinning process, a supplementary voltage supply is conducive to separating nanofiber bundles into random-oriented nanofibers. Electro-blown spun papers possess an ultrahigh efficiency of 99.99% with a reduced areal density of 0.9 g m<sup>–2</sup>. These PA-66 papers can be used in a variety of applications, such as reusable personal protective equipment, industrial waste gas treatment, and central ventilation purification systems.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c04253?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c04253</a>.The facile peeling-off process (Video S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04253/suppl_file/am1c04253_si_001.mp4">MP4</a>)Viscosity curves of the PA-66 solution (Figure S1); shear stress curves of the PA-66 solution (Figure S2); SEM images of a film nanofiber blow-spun from a 20% PA-66 solution at a solution feeding rate of 8 and 10 mL h<sup>–1</sup> with the gas pressure of 50 kPa (Figure S3); SEM images of blow-spun PA-66 nanofibers at different gas pressures of 40, 50, and 60 kPa (Figure S4); the optical image of the PA-66 nanofiber aerogel (Figure S5); TG, DTG, and DSC curves of the PA-66 sample (Figure S6); and SEM images of blow-spun PA-66 nanofibers after being heated at 200, 220, and 240 °C for 2 h in a muffle furnace (Figure S7) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c04253/suppl_file/am1c04253_si_002.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology