Abstract:The structure of a TBC is locally tailored oriented by regional performance requirements to balance the tradeoff between high thermal insulation and long lifespan. The design‐matched TBCs exhibited double the lifespan of the conventional sample with comparable thermal insulation. Mechanism responsible for the long life span was revealed based on healing of the intrinsic two‐dimensional pores and formation of new large pores. Thermal barrier coatings (TBCs) require both a porous structure to effectively prevent heat flux and a considerably dense structure to resist cracking for long‐term protection. These opposite requirements are difficult to achieve in conventional TBCs, which often exhibit uniform structures across their thickness. In fact, the main requirements of a coating vary with thickness owing to differential service conditions. In this study, the structure of a TBC is locally tailored to meet regional performance requirements. First, the load‐bearing conditions across the thickness are investigated in a simulation study. Resulting from multiple causes, the bottom region must bear a larger stress than the top region, which is directly exposed to heat flux. Therefore, the structure should be crack‐resistant in its bottom region and thermally insulating in its top region. Second, region‐function‐matching TBCs were prepared, and their performances were evaluated through isothermal cycling and thermal exposure tests. Results show that the TBCs with matching design exhibited double the lifespan of the conventional samples, whereas the thermal insulation was comparable. Finally, the structural evolutions were examined in different regions to analyze the failure behaviors of the TBCs. Healing of the intrinsic two‐dimensional pores and formation of the new large pores mainly account for the changes in thermal and mechanical properties of the TBCs. Overall, this region‐function‐matching design is expected to balance the tradeoff between high thermal insulation and long lifespan.

Durable TBCs with Self-Enhanced Thermal Insulation Based on Co-Design on Macro- and Microstructure

Achieving Self-Enhanced Thermal Barrier Performance Through a Novel Hybrid-Layered Coating Design

A matching design co-enhancing thermal barrier and thermal cyclic performances of sintering-resistant coatings

Tailoring Sintering-Resistant Thermal Barrier Coatings by Considering Critical Healing Width of Two-Dimensional Interlamellar Pores

Self-Enhancing Thermal Insulation Performance of Bimodal-Structured Thermal Barrier Coating

Low-thermal-conductivity thermal barrier coatings with a multi-scale pore design and sintering resistance following thermal exposure

Matching Design of Thickness Ratio to Extend the Lifespan of Double-Layered Thermal-Barrier Coatings

Tailoring degradation-resistant thermal barrier coatings based on the orientation of spontaneously formed pores: From retardation to self-improvement

Sintering Induced the Failure Behavior of Dense Vertically Crack and Lamellar Structured TBCs with Equivalent Thermal Insulation Performance

Region‐function‐matching design for YSZ‐based thermal barrier coatings enables long thermal cyclic lifespan

Multi-Scale Structural Design and Advanced Materials for Thermal Barrier Coatings with High Thermal Insulation: A Review

A comprehensive sintering mechanism for TBCs-Part I: An overall evolution with two-stage kinetics

Multiscale Pores in TBCs for Lower Thermal Conductivity

Multi-layered Thermal Barrier Coatings Fabricated by Plasma-Spraying and Dry-Ice Blasting: Microstructure Characterization and Prolonged Lifetime

Failure Mechanism and Cracking-Resistant Design of Thermal Barrier Coatings with Long Life Span

A Comprehensive Mechanism for the Sintering of Plasma-Sprayed Nanostructured Thermal Barrier Coatings

Microstructural Design and Thermal Cycling Performance of a Novel Layer-Gradient Nanostructured Sc2O3–Y2O3 Co-Stabilized ZrO2 Thermal Barrier Coating

Thermal Gradient Cyclic Lifetime of DVC and Lamellar Thermal Barrier Coatings with Equivalent Thermal Insulation Performance

Strain/sintering Co-Induced Multiscale Structural Changes in Plasma-Sprayed Thermal Barrier Coatings

Extending interfacial toughness and thermal cycling lifetime of thermal barrier coatings via interfacial 3D pattern

Improved the Durability of Thermal Barrier Coatings with Interface Modified by Three‐Dimensional Mesh Patterns