The Effects of Li Addition on the Microstructure, Mechanical Properties, in Vitro Corrosive Behavior and Biocompatibility of Biodegradable Zn-0.5sr Alloy
Jiao Zhang,Jing Yang,Qinglin Li,Huimin Qiao,Changjun Han,Zhi Dong
DOI: https://doi.org/10.2139/ssrn.4618619
2023-01-01
Abstract:Recently, there has been a surge of interest in the field of Zinc-based alloys because of their exceptional compatibility with living organisms and their moderate rate of degradation. However, the lower strength and poor plasticity severely limit their future applicability. To enhance and optimize the mechanical characteristics, as well as meet the corrosion criteria following implantation, alloying, extrusion, and rolling techniques are extensively employed in the processing of Zn-based alloys. This study aims to comprehensively examine the impact of incorporating 0.6 wt.% Li and utilizing extrusion shaping on the microstructure, mechanical attributes, and corrosive tendencies of the Zn-0.5Sr alloy employed in biomedical applications. The microstructure evolution revealed that the average size of α-Zn grains significantly decreased from 6.7 μm to 5.3 μm when 0.6 wt.% Li was added to Zn-0.5Sr alloy. Furthermore, Zn-0.5Sr-0.6Li alloy had more texture structure along the extrusion direction after extrusion deformation than that of Zn-0.5Sr alloy. The tensile tests demonstrated that the extruded Zn-0.5Sr-0.6Li alloy had superior tensile strength and ductility. The Zn-0.5Sr alloy, in its as-extruded state, demonstrated mechanical properties characterized by a yield strength (YS) of 125 MPa, an ultimate tensile strength (UTS) of 173 MPa, and an elongation (El) of approximately 10.85%. This alloy, after undergoing the extrusion process, displayed a substantial resistance to deformation, withstanding forces up to 125 MPa before any permanent deformation occurred. Moreover, it exhibited impressive tensile strength, reaching a maximum value of 173 MPa before fracturing. Additionally, the material exhibited a notable elongation of approximately 10.85%, indicating its ability to undergo plastic deformation before failure. These results highlight the promising mechanical properties of the Zn-0.5Sr alloy, making it a potential candidate for various applications requiring both strength and ductility. However, the YS and UTS of as-extruded Zn-0.5Sr-0.6Li alloy were sharply improved to 378 and 541 MPa, but the plasticity occurred to deterioration and the El decreased to 7.69%. Moreover, the electrochemical test outcomes exhibited that the corrosion rate of the Zn-0.5Sr alloy, which was subject to extrusion, amounted to 4.098 mm/a. Conversely, the incorporation of 0.6 Li into the Zn-0.5Sr alloy and subsequent extrusion resulted in a substantial reduction in the corrosion rate to 2.146 mm/a. After subjecting the as-extruded Zn-0.5Sr alloy and the as-extruded Zn-0.Sr-0.6Li alloy to a 30-day period of in vitro immersion corrosion, it was observed that the corrosion rate of the former was measured to be 1.987 ± 0.007 mm/a, whereas the corrosion rate of the latter was found to be 1.216 ± 0.015 mm/a. This significant disparity in corrosion rates indicates that the addition of Li to the Zn-0.5Sr alloy effectively enhances its corrosion resistance. The incorporation of Li into the alloy matrix imparts beneficial properties that shield the material from detrimental corrosion processes, potentially extending its lifespan and applicability in various environments where corrosion resistance is of utmost importance. These findings underscore the potential of the Zn-0.Sr-0.6Li alloy is a corrosion-resistant material with a wide range of practical applications. Furthermore, by conducting in-vitro cell experiments, it was substantiated that the introduction of Li into