Tin Assisted Fully Exposed Platinum Clusters Stabilized on Defect-rich Graphene for Efficient Dehydrogenation Reaction
Jiayun Zhang,Yuchen Deng,Xiangbin Cai,Yunlei Chen,Mi Peng,Zhimin Jia,Zheng Jiang,Pengju Ren,Siyu Yao,Jinglin Xie,Dequan Xiao,Xiaodong Wen,Ning,Wang,Hongyang Liu,Ding Ma
2019-01-01
Abstract:Atomically dispersed Pt clusters and single-site Sn are fabricated together on the coreshell nanodiamond@graphene (ND@G) hybrid support (a-PtSn/ND@G). This unique atomically dispersed Pt clusters can dramatically inhibit the side reactions and present excellent catalytic performance in direct dehydrogenation of n-butane at 450 °C, with >98% selectivity toward olefin products, in comparison with that of Al2O3 supported Pt3Sn alloy nanoparticles (Pt3Sn/Al2O3), due to the efficient utilization of Pt atoms and facile desorption of olefin. The combined results of density functional theory (DFT) calculation, HAADF-STEM and X-ray absorption fine structure (XAFS) results provide substantial insights that Pt clusters can be atomically dispersed and stabilized on the ND@G support by the assistance of single-site Sn species as a diluent agent and by the formation of Pt-C bond between Pt clusters and defective graphene nanoshell. Introduction Light olefins as one of the widely used feedstock in chemical industry are important building blocks for synthesis of chemical products.1-2 Direct dehydrogenation (DDH) of light alkane as a typically industrial production process of these olefins undergoes an endothermic process, which requires high temperature to obtain satisfactory conversion rate and olefin yields, and it generally leads to serious catalyst deactivation by sintering of active sites and coking at higher reaction temperature.1, 3 To-date, alumina-supported PtSn catalyst (PtSn/Al2O3) for dehydrogenation of light olefin is of wide research interest. As for PtSn/Al2O3 catalyst, the addition of Sn is crucial to obtain a better catalytic property in higher olefin selectivity and the formation of alloy Pt3Sn can deliver better catalyst activity, while fast deactivation is still a main problem because the sintering of Pt3Sn nanoparticles (NPs) cannot be effectively inhibited during dehydrogenation or reversed during regeneration process. Therefore, the development of highly dispersed and stabilized Pt-based catalyst is still urgent. 4-7 In general, the support of catalyst plays an important role in Pt-based catalyst.6, 810 Among the various supports, nanocarbons such as graphene-like materials have drawn much attention for their feasible fabrication of single site atom catalyst 11-17and exhibit distinct catalytic performance in various reactions.18-21 Nanodiamond is a unique nanocarbon material. After a facile thermal treatment, its surface can be reconstructed into an ultrathin, curved and defective sp2 graphene nanoshell reinforced by a sp3 diamond nanocore (ND@G), which is beneficial for stabilizing metal NPs, through a strong metal-support interaction (MSI) between metal NPs and graphene nanoshell. 22-23 Herein, we report a new Pt-Sn catalyst that consists of single-site Sn and atomically dispersed Pt clusters together anchored on the ND@G hybrid support (aPtSn/ND@G). The as-prepared a-PtSn/ND@G catalyst provides enhanced DDH performance of n-butane in comparison with that of Al2O3 supported Pt3Sn alloy nanoparticles (Pt3Sn/Al2O3) which is normally considered responsible for higher activity in DDH reaction.24 Multi-technique characterizations and DFT calculations results show that single-site Sn species deliver a dilution effect and Pt clusters are atomically dispersed among them through the linkage of Pt-C bond between Pt and graphene nanoshell. The as-prepared a-PtSn/ND@G catalyst dramatically inhibits the side reaction and shows distinct catalytic performance in DDH of n-butane at low temperature, resulting from the efficient use of Pt atom and the lower energy barrier for desorption of butene over these unique Pt clusters. Results and discussion Figure 1. HADDF-STEM characterization of a-PtSn/ND@G. A) STEM images showing the homogeneous distribution of Pt clusters and B-E) the atomic dispersion of Pt and Sn). For clarity, some Sn and Pt atoms in image B are marked out by green and red circles according to the Z-contrast mechanism, respectively. (The scale bars in B-E are 0.5 nm). F-I) Energy-dispersive X-ray (EDX) spectroscopy showing the composition maps of the a-PtSn/ND@G. The aberration-corrected high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) was employed to study the dispersion of Pt and Sn on ND@G (Figure 1). Notably, Pt clusters were homogeneously decorated on ND@G as the light dots marked in Figure 1 A without any existence of Pt particles. The representative atomic images (Figure 1 B-E) showed that several Pt atoms formed a cluster as single atomic layer (Figure S2), while the single-site Sn atoms surrounded the Pt cluster in a random manner. The energy-dispersive X-ray (EDX) spectroscopy results (Figure 1 F-I) confirmed the coexistence and distinct distribution forms of Pt (red, clusters) and Sn (green, homogenous dispersion at atomic scale) on the support carbon (blue). A further H2/O2 titration measurement was performed (Table S1) and the result showed that for a-PtSn/ND@G, the dispersion of Pt is 99.2%, which is close to 100%, suggesting that almost all the Pt atoms are exposed on the surface of support. This result obviously supports the conclusion that ND@G can afford atomically dispersed Pt clusters. By contrast, Pt3Sn alloy particles (d≈0.406nm, the lattice distance of Pt3Sn (100) is 4.004 (PDF#65-0958)) on Al2O3 are observed rather than atomically dispersed Pt clusters (Figure S3 A-E). Composition analysis of Pt3Sn/Al2O3 by EDX confirms the alloying of Sn and Pt (Figure S3 F-I). The dispersion of Pt on Pt3Sn/Al2O3 is 74.7%, which is in good agreement with the calculation result from a theoretical model of 4 nm Pt3Sn nanoparticle (Table S1). Figure 2. A) FT-EXAFS profiles for a-PtSn/ND@G, Pt3Sn/Al2O3, Pt foil and PtO2. B) Wavelet transform (WT) analysis of a-PtSn/ND@G and C) Pt3Sn/Al2O3. D) XANES data characterizing Sn foil, a-PtSn/ND@G, and SnO2. E) The optimized structure of Pt3 cluster embedded into graphene (Pt3-graphene) from top and side view, where the Pt-C bonds length is: 1.946, 1.977, 1.969, 2.046 and 2.301 . The structure and the average coordination environment of Pt and Sn species were investigated by the extended X-ray absorption fine structure (EXAFS) spectroscopy. The Fourier-transformed (FT) k3-weighted EXAFS at the Pt L3-edge is shown in Figure 2A. For a-PtSn/ND@G catalyst, the distinct peak at 1.6 and the shoulder peak at 2.6 can be observed, corresponding to Pt-C and Pt-Pt first coordination shell, respectively. As for Pt3Sn/Al2O3, the main peak at 2.6 belongs to Pt-Pt and Pt-Sn first coordination shell. Wavelet transformation (WT) of Pt L3-edge EXAFS oscillations further illustrate the dispersion of Pt. Notably, the maximum WT intensity near 1.6 belongs to Pt-C contribution and another maximum at 2.6 corresponds to Pt-Pt contribution (Figure 2B), indicating the existence of Pt clusters anchored on the support by Pt-C in a-PtSn/ND@G catalyst. By contrast, only a maximum at 2.6 Å can be observed for Pt3Sn/Al2O3 (Figure 2C), revealing the formation of the Pt3Sn alloy NPs on Al2O3 support. The detailed parameters of these two samples are shown in Table S5, Figure S5 and Figure S6. The collected results show that for a-PtSn/ND@G catalyst, the average coordination number (CN) of Pt-C contribution is 2.2, while the average CN of Pt-Pt contribution is only 1.8, which is much lower than that in Pt foil (CN of Pt-Pt is 12) and bulk PtO2 (CN of Pt-O is 6) 25, confirming the presence of ultra-small Pt clusters on the ND@G. Meanwhile, the PtSn contribution is absent, indicating that Pt species do not form Pt-Sn alloy. In addition, two Sn-O-Sn shell, with an average CN of 1.2 at a bond distance of 3.37 Å and 4.8 at a bond distance of 3.89 Å, are also presented and denoted as Sn-O-Sn1 and Sn-O-Sn2. The Sn-O coordination number is 5.9 at a bond distance of 2.05 Å and there is no Sn-Sn contribution. All these results further prove that the Sn species as single sites are also atomically dispersed on ND@G. Furthermore, the X-ray absorption near edge structure data indicates the existence of Sn as cationic species (Figure 2D). For Pt3Sn/Al2O3, the presence of Pt-Sn coordination, the ratio of CN of Pt-Pt and Pt-Sn and the similar bond length of Pt-Pt and Pt-Sn suggest the existence of Pt-Sn alloy. In order to further clarify the local coordination structure of Pt species, the density functional theory (DFT) calculation was used to investigate different bonding models of Pt-(C/O) on ND@G. As shown in Figure 2E, the optimized geometry of the Pt3-graphene yields average bond length (2.05 Å) that is in good agreement with the experimental values of the Pt-C bond length (2.02±0.03 Å) in the first coordination shell. In addition, we exclude the possible PtOx species embedded on the graphene in H2 atmosphere. As shown in Table S8-S10 and the reaction change of Gibbs free energies of Pt3Ox-graphene in supporting information, oxygen can be captured easily by H2 in the reaction condition. So, the most stable structure under reaction condition should be Pt3 cluster stabled by graphene, which is applied in the further DFT calculations. The electronic states of Pt species were investigated by X-ray photoelectron spectroscopy (XPS). As shown in Figure S7A and Table S2, Pt is completely in metallic state in Pt3Sn/Al2O3 sample after reduction since the peak centered around 71.1eV (Pt 4f7/2) corresponds to Pt.26-27 For a-PtSn/ND@G, the peak of Pt shows an upward shift trend in the binding energy (BE) compared to that of Pt3Sn/Al2O3 (71.9eV vs 71.1 eV), which illustrates that Pt clusters trend to electron-deficient state in a-PtSn/ND@G. The XPS spectra of Sn is also presented in Figure S7 B, revealing that in a-PtSn/ND@G, Sn species in oxidation state Sn (II, IV), Thus, all the results above demonstrate that in a-PtSn/ND@G catalyst, several Pt atoms form a cluster of single atomic layer with electron-deficient, which is surrounded randomly by singlesite Sn atoms as the dilute ag