Development of novel Fe-based bulk metallic glasses with excellent wear and corrosion resistance by adjusting the Cr and Mo contents
Chengwu Zhang,Qiang Li,Lei Xie,Guan Zhang,Baoxia Mu,Chuntao Chang,Hongxiang Li,Xu Ma
DOI: https://doi.org/10.1016/j.intermet.2022.107801
IF: 4.075
2022-12-11
Intermetallics
Abstract:In this work, a series of novel Fe 80–x–y Cr x Mo y P 10 C 7 B 3 (x = 0, y = 0; x = 0, y = 4; x = 5, y = 4; x = 15, y = 4; x = 20, y = 4; x = 15, y = 8 in at.%; denoted as Cr x Mo y ) bulk metallic glasses (BMGs) with critical diameters in the range 1.0–2.5 mm were fabricated. The effect of Cr and Mo contents on the glass forming ability (GFA), thermal stability, mechanical properties, corrosion behavior, and wear performance of the these Fe-based BMGs were systematically investigated. A partial substitution of Fe by Cr and Mo was found to enhance the GFA of the Fe-based BMGs. The sample Cr 15 Mo 4 exhibited the maximum critical diameter (2.5 mm), maximum temperature range of the supercooled liquid phase (55 K), and highest activation energy for the primary crystallization process (184 kJ·mol −1 ). Uniaxial compression and microhardness tests revealed that the compressive strength and Vickers microhardness of the Fe-based BMGs were in the range 3.0–3.7 GPa and 794–958 HV 0.1 , respectively, and increased with increasing Cr/Mo content. Electrochemical tests in a 3.5 wt.% NaCl solution showed that the Fe-based BMGs exhibited a significantly higher corrosion resistance than 316L stainless steel (316L SS) and 304L stainless steel (304L SS). The corrosion resistance of the Fe-based BMGs generally improved with increasing Cr/Mo content. The sample Cr 15 Mo 4 exhibited the highest corrosion resistance with a self-corrosion and passivation current density ∼10 −8 A·cm −2 and ∼10 −6 A·cm −2 , respectively. X-ray photoelectron spectroscopy of the samples revealed that compared to Cr 15 Mo 4 , there was a higher proportion of defective high-valence metal cation (Fe 3+ , Cr 6+ , and Mo 6+ ) oxides and a lower proportion of stable low-valence metal cation (Fe 2+ , Cr 3+ , and Mo 4+ ) oxides in the passive films of Cr 20 Mo 4 and Cr 15 Mo 8 . This explains the reason why adding more than 15 at.% Cr and 4 at.% Mo degrades the corrosion resistance of the Fe-based BMGs. The dry sliding wear test demonstrated that the Fe-based BMGs exhibited significantly better wear performance than 316L SS and 304L SS. The wear rate and coefficient of friction of the Fe-based BMGs decreased with increasing Cr/Mo content. The sample Cr 15 Mo 8 exhibited the lowest wear rate and coefficient of friction of 0.98 × 10 −5 mm 3 ·N −1 ·m −1 and 0.38, respectively. The Fe-based BMGs synthesized in this work, especially Fe 61 Cr 15 Mo 4 P 10 C 7 B 3 , exhibited a high GFA and excellent corrosion and wear resistance. Therefore, they have immense potential for various engineering applications.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering