New Insights on Nucleation and Transformation Process in Temperature-Induced Martensitic Transformation

Jinliang Wang,Xiaohui Xi,Yong Li,Chenchong Wang,Wei Xu

DOI: https://doi.org/10.1016/j.matchar.2019.03.023

IF: 4.537

2019-01-01

Materials Characterization

Abstract:Understanding mechanisms of the nucleation and transformation sequence is of critical importance to control temperature-induced martensitic transformations and hence retained austenite. In the present work, quasi-in situ Electron Backscattering Diffraction and Transmission Electron Microscopy were employed to investigate the nucleation and transition in a prototype austenitic stainless steel. Detailed evidence was provided, that nucleation could occur on new defects generated during cryogenic treatment, and not just on pre-existing defects. Moreover, transformation follows both austenite -> epsilon-martensite -> alpha'-martensite and austenite -> alpha'-martensite routes, their associated mechanisms, and crystallographic characteristics were analysed. These new insights could provide further guidelines for the optimization and modelling of martensitic transformation.