Abstract:Intermittent oil-water wetting can have a significant effect on the internal corrosion of steel pipelines. This paper presents a combined experimental and molecular modeling study of several influential factors on the surface properties and corrosion behavior of mild steel in CO2 environments. The influence of different model oils (LVT-200 and Aromatic-200) and select surface-active compounds (myristic acid, cyclohexane butyric acid, and oleic acid) on the corrosion behavior of carbon steel during intermittent oil-water wetting was determined by measuring the corrosion rate after intermittent wetting cycles. The interfacial tension measurements were performed to study the incorporation of the oil phase along with surface-active molecules in the protective layer formed on the specimen surface. Results showed that the interfacial tension for an aromatic oil-water interface is lower than that for an aliphatic oil-water interface. To understand this result, molecular dynamics simulations of oil-water interfaces were performed in the presence of surface-active molecules and different oils to analyze the structure of the layer formed at the interface. The simulations supported the hypothesis that aromatic molecules are less structured at the interface, which results in the incorporation of more water molecules into the protective layer formed at the steel surface, causing a higher corrosion rate. On the other hand, the simulations revealed that myristic acid in an aliphatic oil forms a well-aligned structure at the interface, devoid of any water molecules. This is in agreement with the hypothesis that the linear molecular structure of myristic acid favors the alignment of molecules at an aliphatic oil-water interface, resulting in a lower interfacial tension and more effective corrosion mitigation as compared to the other two nonlinear compounds tested. It is concluded that an important factor controlling the corrosion behavior is the molecular structure of the oil-water interface, which is adopted by the steel surface layer through the Langmuir-Blodgett process.

Corrosion Mitigation Behavior of an Alternately Wetted Steel Electrode in Oil/water Media

Understanding the Corrosion Behaviour of Steel Under Alternate Oil/Water Wetting with Different Oil Viscosities

Corrosion Behavior of a Low-Carbon Steel in Simulated Marine Splash Zone

Experimental study on corrosion of 20# steel in oil-water stratified liquids based on wire beam electrode technique

Study of anti-contamination performance of temporarily protective oil coatings using wire beam electrode

Influence of the Dissolved Oxygen Concentration in Artificial Seawater on the Corrosion Behavior of Q235 Mild Steel

Preparation of Superhydrophobic Coating on X80 Steel and Its Corrosion Resistance in Oilfield Produced Water

Study on corrosion characteristics of Q235 steel in seawater, soil and dry-wet alternating environments focusing on Shengli oilfield

Experiments and Molecular Simulations to Study the Effect of Surface-Active Compounds in Mixtures of Model Oils on CO2 Corrosion during Intermittent Oil-Water Wetting

Visualizing and understanding corrosion evolution beneath a condensed droplet using the multi-electrode array

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

Effect of Ochrobactrum sp. on the Corrosion Behavior of 10MnNiCrCu Steel in Simulated Marine Environment

The Corrosion Behavior of Steel Exposed to a DC Electric Field in the Simulated Wet-Dry Cyclic Environment

Corrosion Behavior of Long-Time Immersed Rusted Carbon Steel in Flowing Seawater

Corrosion Behavior of High-Strength Low-Alloy Steel in High-Temperature Water with Zinc and Aluminum Simultaneous Injection

Corrosion Assessment and Characterization of Aerospace-Bearing Steels in Seawater and Ester-Based Lubricants

Influence of Ultraviolet Light and Alternating Wet-Dry Environments on the Corrosion Behavior of Weathering Steels

Alternate immersion improves corrosion inhibition efficiency of Halomonas titanicae towards EH40 steel

Errosion-Corrosion Critical Performance of Surface Nanocrystalline 20 Carbon Steel in Condensate Water

Accelerated corrosion of low carbon steel by oscillatory acidic streams generated with a bio-inspired claw device

Interaction of Mechanical and Electrochemical Factors During Corrosion-Fatigue of Fe-26cr-1mo Stainless-Steel in 1m H2so4 Solution