A "Ship-in-a-bottle" Strategy to Fabricate Highly Crystallized Nanoporous Graphitic C3N4 Microspheres under Pressurized Conditions

Zongzhao Sun

DOI: https://doi.org/10.1039/c9ta00151d

IF: 11.9

2019-01-01

Journal of Materials Chemistry A

Abstract:Highly crystallized nanoporous g-C3N4 microspheres were obtained by confined thermal polymerization of the precursor inside hollow silica microspheres under a pressurized atmosphere.

What problem does this paper attempt to address?

Highly crystalline carbon nitride hollow spheres with enhanced photocatalytic performance

Yang Li,Dainan Zhang,Jiajie Fan,Quanjun Xiang

DOI: https://doi.org/10.1016/s1872-2067(20)63684-1

IF: 16.5

2021-04-01

Chinese Journal of Catalysis

Abstract:Graphitic carbon nitride (g-C3N4) has emerged as a remarkably promising photocatalyst for addressing environmental and energy issues; however, it exhibits only moderate photocatalytic activity because of its low specific surface area and high recombination of carriers. Preparation of crystalline g-C3N4 by the molten salt method has proven to be an effective method to improve the photocatalytic activity. However, crystalline g-C3N4 prepared by the conventional molten salt method exhibits a less regular morphology. Herein, highly crystalline g-C3N4 hollow spheres (CCNHS) were successfully prepared by the molten salt method using cyanuric acid-melamine as a precursor. The higher crystallization of the CCNHS samples not only repaired the structural defects at the surface of the CCNHS samples but also established a built-in electric field between heptazine-based g-C3N4 and triazine-based g-C3N4. The hollow structure improved the level of light energy utilization and increased the number of active sites for photocatalytic reactions. Because of the above characteristics, the as-prepared CCNHS samples simultaneously realized photocatalytic hydrogen evolution with the degradation of the plasticizer bisphenol A. This research offers a new perspective on the structural optimization of supramolecular self-assembly.

chemistry, physical,engineering, chemical, applied
One-pot synthesis of porous g-C3N4 nanosheets with enhanced photocatalytic activity under visible light

Cunlu Wang,Guangwei Zhang,Han Zhang,Zihao Li,Yeqian Wen

DOI: https://doi.org/10.1016/j.diamond.2021.108416

IF: 3.806

2021-06-01

Diamond and Related Materials

Abstract:Porous graphitic carbon nitride nanosheets (PMCNS) photocatalyst with a specific surface area of 92.75 m2 g−1 was prepared by ammonium carbonate guide structure in a one-pot strategy. Compared with bulk graphitic carbon nitride (MCN), the pores in the PMCNS formed by curling and sealing of the lamella provide more active sites, which promote charge separation and transfer, and inhibit the recombination of photoexcited electron and hole pairs. To confirm our strategy, the photocatalytic degradation of rhodamine B (RhB) and hydrogen evolution ability of PMCNS under visible light were performed, and a significant enhancement was observed, the efficiencies are 12.8 and 3.8 times that of MCN, respectively. This work provides an approach for reconstruction of graphitic carbon nitride (g-C3N4) structure to improve the photocatalytic oxidation and reduction capabilities under visible light.

materials science, multidisciplinary,physics, applied, condensed matter, coatings & films
Template-free Preparation and Characterization of Nanoporous G-C3n4 with Enhanced Visible Photocatalytic Activity

Qifeng Cai,Jianchao Shen,Yu Feng,Qianhong Shen,Hui Yang

DOI: https://doi.org/10.1016/j.jallcom.2014.12.013

IF: 6.2

2014-01-01

Journal of Alloys and Compounds

Abstract:A novel method was proposed to fabricate nanoporous g-C3N4 through high energy ball milling process followed by protonation treatment. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), Brunauer-Emmett-Teller (BET), laser particle analysis, UV-vis diffuse reflection spectroscopy (DRS), photoluminescence spectroscopy, electron paramagnetic resonance (EPR), and photoelectrochemical experiment were adopted to analyze the structure and properties of nanoporous g-C3N4 photocatalyst. The photocatalytic activities of the as-prepared samples were also evaluated by decomposing Congo Red (CR) and Rhodamine B (RhB) in aqueous solution under visible light illumination. The results show that the as-prepared nanoporous g-C3N4 exhibits high specific surface area, which is about 8.8 times as high as that of the original bulk one, and also shows more efficient exciton collection and charge transfer. Therefore, the visible photocatalytic activity of g-C3N4 is significantly improved, and the decomposition rate of congo red is increased from 0.03 to 0.32 h(-1). Furthermore, this photocatalyst also displays a selective feature in photocatalysis due to its positive surface charges determined by protonation treatment. (C) 2014 Elsevier B.V. All rights reserved.
"Alternated Cooling and Heating" Strategy Enables Rapid Fabrication of Highly-Crystalline G-C3n4 Nanosheets for Efficient Photocatalytic Water Purification under Visible Light Irradiation

Shifei Kang,Lu Zhang,Maofen He,Yuanyi Zheng,Lifeng Cui,Di Sun,Bing Hu

DOI: https://doi.org/10.1016/j.carbon.2018.05.010

IF: 10.9

2018-01-01

Carbon

Abstract:Highly-crystalline 2-dimensional (2D) graphitic carbon nitride (g-C3N4) nanosheets with low structural imperfection usually possess high photocatalytic activity that benefits from the suppressed electron ehole recombination. However, the conventional exfoliation strategy is incapable for fast and clean preparation of such highly-quality g-C3N4 nanosheets from their bulk-type counterparts. Herein, highly-crystalline few-layer g-C3N4 nanosheets were synthesized only within 10 min by judiciously combining flash freezing and microwave-assisted thermo-exfoliation. Physicochemical characterization showed the ultrathin g-C3N4 nanosheets had high crystallinity, narrowed band gap (2.62 eV), enlarged specific surface area (88.59m(2)/g) and enhanced electron transport ability. The quasi-2D few-layer g-C3N4 nanosheets were more efficient than bulk g-C3N4 in photocatalytic water purification and disinfection, as evidenced by 3-fold enhancement in humic acid photodegradation and fast water disinfection against Escherichia coli under visible-light irradiation. Such improvements were mainly attributed to the reduction of structural defects and enrichment of exposed active sites, which together led to efficient self-suppression of electronehole recombination. These findings provide an inspiration for scale-up and clean production of highly-active 2D materials towards environmental and biological application. (c) 2018 Elsevier Ltd. All rights reserved.
Moderate NaNO2 Etching Enables Easy Crystallinity Optimization of G-C3n4 with Superior Photoreduction Performance

Lifeng Cui,Zirou Fang,Yanfei Liu,Mengya Chen,Chaochuang Yin,Junjie Wang,Zegao Wang,Mingdong Dong,Shifei Kang,Ping Liu

DOI: https://doi.org/10.1039/c9qi00113a

IF: 7.779

2019-01-01

Inorganic Chemistry Frontiers

Abstract:As a promising visible-light-responsive catalyst, graphitic carbon nitride (g-C3N4) has been widely used in environmental and energy applications owing to its unique semiconducting optoelectronic properties. However, the photocatalytic performance of bulk g-C3N4 synthesized using N-containing precursors via a conventional thermal polycondensation process is generally limited by low crystallinity caused by incomplete polymerization. In addition to forced polymerization under high-pressure conditions, removing the unpolymerized and inactive part of bulk g-C3N4 through controllable etching is another practical way to optimize its crystallinity. Therefore, we developed an economical and general method to fabricate g-C3N4 with high crystallinity and excellent photocatalytic properties, in which cheap sodium nitrite aqueous solution is utilized as a moderate etching agent. The compositions and physiochemical properties of the products were comprehensively investigated by X-ray diffraction, Fourier-transform infrared spectroscopy, ultraviolet visible diffuse reflectance spectroscopy, X-ray photoelectron spectroscopy, N-2 adsorption-desorption, and electrochemical impedance spectroscopy measurements. In addition, ToF-SIMS (time-of-flight secondary ion mass spectrometry), a new surface analysis technology, was also used to determine the surface and structural characteristics of all samples. The obtained g-C3N4 shows ideal high-crystallinity features and excellent charge transfer ability, leading to significantly improved Cr(VI) reduction activity under visible light. Moreover, there is only a low content of nitrite residue (63.3 mg g(-1)) in the final g-C3N4 product, indicating that the method employing NaNO2, which is widely used in the food industry, is safe and waste-free. Therefore, the new controllable NaNO2 etching method is cleaner and more efficient than commonly-used corrosion approaches based on strong acids or strong oxidants, and thus affords a new strategy in the regulation and structural design of various catalysts.
Supermolecule Polymer Derived Porous Carbon Nitride Microspheres with Controllable Energy Band Structure for Photocatalytic Hydrogen Evolution Reaction

Zhengzheng Xie,Qiang Gao,Sajjad Hussain,Jianjun Yang,Qiuye Li

DOI: https://doi.org/10.1002/smll.202309032

IF: 13.3

2023-12-12

Small

Abstract:In this work, porous g‐CN microspheres are synthesized via a simple method with MCA as the intermediates. And the morphology and energy band structure of g‐CN are intimately calcination time‐dependent. The visible‐light HER rate of g‐CN@Pt reaches 10.14 mmol g−1 h−1. The formation and internal mechanism of g‐CN are studied and supplemented by theoretical calculations. Porous graphitic carbon nitride microsphere with large specific surface area and controllable energy band structure is synthesized via a simple method with the supermolecule polymer of melamine‐cyanuric acid (MCA) as the intermediates. The energy band structure and morphology of carbon nitride are closely correlative to the calcination time. And the CN‐20 catalyst fabricated by calcination for 20 h exhibit superior photocatalytic activity of hydrogen evolution reaction (HER) under visible‐light (λ ≥ 420 nm) irradiation. The photocatalytic and photoelectrochemical test results indicate that Pt is the optimum cocatalyst candidate compared with Pd, Ru, and Ag. Meanwhile, the time‐dependent process of the intermediate pyrolysis to carbon nitride and the internal mechanism of photogenerated charge transfer between semiconductors and cocatalyst is investigated and supplemented by theoretical calculations. This work provides a novel and energy band structure controllable manufacture strategy for porous carbon nitride semiconductor with satisfying visible‐light photocatalytic reduction performance.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
Electrostatic self-assembly combined with microwave hydrothermal strategy: construction of 1D/1D carbon nanofibers/crystalline g-C3N4 heterojunction for boosting photocatalytic hydrogen production

Feng Lin,Shuang Zhou,Guohong Wang,Juan Wang,Tengyuan Gao,Yaorong Su,Ching-Ping Wong,Feng Lin,Shuang Zhou,Guohong Wang,Juan Wang,Tengyuan Gao,Yaorong Su,Ching-Ping Wong

DOI: https://doi.org/10.1016/j.nanoen.2022.107432

IF: 17.6

2022-08-01

Nano Energy

Abstract:g-C3N4 (CN) has been widely explored as a visible light photocatalyst. Nevertheless, the low structural ordering of CN suffers from high-density defects that resulting in poor charge separation efficiency. Therefore, increasing the crystallinity of CN is considered to be an efficient approach to enhance its photocatalytic activity. However, crystalline g-C3N4 (CCN) synthesized via ionothermal method exhibits one-dimensional (1D) nanorod structure and is prone to agglomerate due to its high surface energy, giving rise to unsatisfactory performance improvement. Herein, the 1D carbon nanofibers/crystalline g-C3N4 heterojunction photocatalyst (CNF/CCN) is obtained through electrostatic self-assembly combined with microwave heating strategy. The CNF/CCN sample shows an enhanced photocatalytic H2 evolution rate (HER) of 6398 μmol g−1 h−1, which is up to 16.0 and 2.6 times of CN and CCN, respectively. The enhanced HER performance of CNF/CCN is attributed to the improved crystallinity of CN, promoted visible light utilization, large specific surface area and efficient charge transfer across the interface between CNF and CCN. This work conveys a simple and general method for crystallinity and activity enhancement for a wide range application of CN.

materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology
Nanoporous Graphitic Carbon Nitride With Enhanced Photocatalytic Performance

Jing Xu,Yajun Wang,Yongfa Zhu

DOI: https://doi.org/10.1021/la402268u

IF: 3.9

2013-01-01

Langmuir

Abstract:Nanoporous g-C3N4 (npg-C3N4) with high surface area was prepared by a bubble-templating method. A higher calcination heating rate and proportion of thiourea can result in a larger surface area and better adsorption and photodegradation activities of npg-C3N4. Compared with the bulk g-C3N4, the adsorption capacity for the target pollutants and photocatalytic degradation and photocurrent performances under visible light irradiation of npg-C3N4 were greatly improved. The optimal photodegradation activity of npg-C3N4 was 3.4 times as high as that of the bulk g-C3N4. The enhanced activities of npg-C3N4 can be attributed to the larger number of surface active sites, improved separation of photogenerated electron-hole pairs, and higher efficiency of charge immigration.
“Carbon Diffusion” Engineered Carbon Nitride Nanosheets for High-Efficiency Photocatalytic Solar-to-fuels Conversion

Ruijie Chen,Zhiqiang Zhang,Jun Wu,Xueru Chen,Lei Wang,Haotian Yin,Hongping Li,Jing Ding,Hui Wan,Guofeng Guan

DOI: https://doi.org/10.1016/j.renene.2022.08.014

IF: 8.7

2022-01-01

Renewable Energy

Abstract:The fabrication of graphitic carbon nitride (g-C3N4) has received much attention for its superior photoelectronic properties, it remains a remarkable challenge with a feasible methodology. Herein, inspired by carburization, a novel method with carbon diffusion was proposed to prepare g-C3N4 nanosheets (CNNS). The carbon diffusion was caused by the gradient difference in carbon concentration between the gaseous environment and the C15 (mild steel with low carbon content) during thermal polymerization. Eventually, the CNNS with approximately 1.5 nm thickness was successfully fabricated and exhibited larger surface area (98.08 m(2) g(-1)), which was 15.42 times higher than that of bulk g-C3N4(BCN). In the evaluation of photocatalytic CO2 reduction activity, the CH3OH formation rate over CNNS (2.10 mu mol g(-1) h(-1)) was 3.28 times greater than BCN. Meanwhile, the designed CNNS exhibited dramatic improvement on H-2 evolved rate (HER) of 2507.02 mu mol g(-1) h(-1), which was 6.99 times higher than BCN. More importantly, the C15 possessed the advantage of 10 times recycled to use for the fabrication of CNNS accompanied by a moderate decrease of HER. Moreover, the density functional theory (DFT) calculations were carried out based on the results. This work highlights an ingenious tactic with carbon diffusion for preparing CNNS towards renewable solar energy conversion.
2D Porous N-Deficient G-C3n4 Nanosheet Decorated with CdS Nanoparticles for Enhanced Visible-Light-Driven Photocatalysis

Hui Liu,Dang-guo Cheng,Fengqiu Chen,Xiaoli Zhan

DOI: https://doi.org/10.1021/acssuschemeng.0c06004

IF: 8.4

2020-01-01

ACS Sustainable Chemistry & Engineering

Abstract:Graphitic carbon nitride (g-C3N4), as a promising visible-light-driven photocatalyst, has attracted extensive attention. However, its photocatalytic performance is limited by its weak light absorption and fast recombination of charge carriers. Herein, a two-dimensional (2D) porous N-deficient g-C3N4 nanosheet (CNNS) was fabricated through molten salt-assisted thermal polycondensation. The remarkable porous nanosheet structure together with the N-deficiency of CNNS played multiple roles, causing a higher specific surface area, better hydrophilicity, and narrowed band gap, thus enabling extended visible light absorption and improved photogenerated charge separation efficiency. As a consequence, the noble-metal-free photocatalyst formed using CNNS and CdS nanoparticles exhibited a significantly enhanced visible-light-driven photocatalytic H-2 production rate of 326 mu mol h(-1) (CdS/CNNS), which is about 8.8 times higher than that of a bulk-g-C3N4-based CdS/BCN photocatalyst (37 mu mol h(-1)). Moreover, with a relatively low Pt content (1 wt %) as a cocatalyst, the H-2 evolution rate further increased up to 2323 mu mol h(-1) (Pt-CdS/CNNS). This work is expected to be helpful in fabricating efficient g-C3N4 photocatalysts.
A Template Induced Method to Synthesize Nanoporous Graphitic Carbon Nitride with Enhanced Photocatalytic Activity under Visible Light

Qianjing Fan,Jianjun Liu,Yingchun Yu,Shengli Zuo

DOI: https://doi.org/10.1039/c4ra12033g

IF: 4.036

2014-01-01

RSC Advances

Abstract:A template induced method was developed to synthesize nanoporous graphitic carbon nitride (npg-CN) by directly heating Triton X-100-modified-melamine sulfate. The effects of the added amount of Triton X-100 and heating temperature on the formation of npg-CN were investigated. The npg-CN samples were characterized by XRD, FT-IR, and elemental analysis; nitrogen adsorption isotherms, SEM and TEM images; and UV-vis DRS and photoluminescence spectra. The results showed that the npg-CN samples possessed a laver-like layered structure with a high surface area (50–135 m2 g−1). Meanwhile, compared to the bulk g-CN (synthesized by directly heating melamine), the npg-CN samples possessed stronger optical absorptions, narrower band gaps, and significantly reduced fluorescence intensity. The photocatalytic activity was investigated by degradation of Rhodamine B under visible light irradiation. As a result, the photodegradation rate of Rhodamine B dye on the npg-CN samples was greatly improved over that on bulk g-CN.
Synthesis of g-C3N4 from Various Precursors for Photocatalytic H2 Evolution under the Visible Light

Pengfei Xia,Guojing Li,Xiaowei Li,Shuhua Yuan,Kang Wang,Dingwang Huang,Yuanpeng Ji,Yunfa Dong,Xiaoqiang Wu,Linyu Zhu,Weidong He,Liang Qiao

DOI: https://doi.org/10.3390/cryst12121719

IF: 2.7

2022-11-27

Crystals

Abstract:Graphitic carbon nitride (g-C3N4) fabricated from different precursors exhibits unique microstructures and photocatalytic performance under visible light. Herein, we synthesized five different microstructures of g-C3N4 by the thermal poly condensation method using guanidine hydrochloride, melamine, urea, dicyandiamide and thiourea as the precursors. The results indicated that g-C3N4 prepared from urea precursor (UCN) has a nanostructure, porous layered structure, large specific surface area, and high separation efficiency of photo generated hole-electron pairs, which showed the best photocatalytic activity among all of the as-prepared samples. As for the lowest cost among the above five precursors, urea is an ideal candidate material for preparing g-C3N4 photocatalyst for a huge potential of wide industrial applications. In addition, Pt or Ni were used as the co-catalyst and loaded onto the g-C3N4 surface for photocatalytic hydrogen production. In comparison with noble metal Pt co-catalyst, Ni co-catalyst is inexpensive and has a significant effect o enhancing the photocatalytic activity under visible light. Therefore, Ni exhibits a considerable prospect to replace noble metal co-catalysts in the photocatalytic reactions.

materials science, multidisciplinary,crystallography
Facile Urea-Assisted Precursor Pre-Treatment to Fabricate Porous G-C3n4 Nanosheets for Remarkably Enhanced Visible-Light-driven Hydrogen Evolution

Jirong Bai,Chaochuang Yin,Haiyang Xu,Gang Chen,Zhijiang Ni,Zhilei Wang,Yaguang Li,Shifei Kang,Zheng,Xi Li

DOI: https://doi.org/10.1016/j.jcis.2018.07.108

IF: 9.9

2018-01-01

Journal of Colloid and Interface Science

Abstract:Hydrogen generation photocatalyzed by low-cost graphite carbon nitride (g-C3N4) is a fascinating and effective route to solve energy crisis, but is mainly limited by the few reactive sites, low carrier separation efficiency and mediocre visible-light utilization. In this work, these limitations were tackled through a facile eco-friendly precursor pretreatment by tuning bulk g-C3N4 into porous structure. This pretreatment restricted agglomeration in the subsequent condensation and created more porous channels for charge carrier transfer and more surface active sites for reaction. The modified g-C3N4 has larger surface area, broader visible-light response, enhanced electron migration capacity and prolonged lifetime of photogenerated carriers. These well-amended g-C3N4 nanosheets possess an average hydrogen evolution rate 5.7 times that of bulk g-C3N4. This work affords a facile, eco-friendly and scalable strategy to design or synthesize other porous materials.
Self-assembled B-doped flower-like graphitic carbon nitride with high specific surface area for enhanced photocatalytic performance

Yi Han,Min Chao,Chunjia Luo,Luke Yan

DOI: https://doi.org/10.1016/j.jcis.2023.11.114

IF: 9.9

2023-11-30

Journal of Colloid and Interface Science

Abstract:Graphitic carbon nitride (g-C 3 N 4 ) is a promising nonmetallic photocatalyst. In this manuscript, B-doped 3D flower-like g-C 3 N 4 mesoporous nanospheres (BMNS) were successfully prepared by self-assembly method. The doping of B element promotes the internal growth of hollow flower-like g-C 3 N 4 without changing the surface roughness structure, resulting in a porous floc structure, which enhances the light absorption and light reflection ability, thereby improving the light utilization rate. In addition, B element provides lower band gap, which stimulates the carrier movement and increases the activity of photogenerated carriers. The photocatalytic mechanism and process of BMNS were investigated in depth by structural characterization and performance testing. BMNS-10 % shows good degradation for four different pollutants, among which the degradation effect on Rhodamine B (RhB) reaches 97 % in 30 min. The apparent rate constant of RhB degradation by BMNS-10 % is 0.125 min −1 , which is 46 times faster compared to bulk g-C 3 N 4 (BCN). And the photocatalyst also exhibits excellent H 2 O 2 production rate under visible light. Under λ > 420 nm, the H 2 O 2 yield of BMNS-10 % (779.9 μM) in 1 h is 15.9 times higher than that of BCN (48.98 μM). Finally, the photocatalytic mechanism is proposed from the results of free radical trapping experiments.

chemistry, physical
Template‐Free Synthesis of Three‐Dimensional Nanoporous Bulk Graphitic Carbon Nitride with Remarkably Enhanced Photocatalytic Activity and Good Separation Properties

Jianchao Shen,Hui Yang,Qianhong Shen,Yu Feng,Qifeng Cai,Huiying Yang

DOI: https://doi.org/10.1002/ejic.201500105

IF: 2.551

2015-01-01

European Journal of Inorganic Chemistry

Abstract:A facile template-free method is presented for the fabrication of three-dimensional (3D) nanoporous bulk graphitic carbon nitride (g-C3N4) with an interconnected framework. Various techniques, namely, X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, transmission electron microscopy, elemental analysis, specific surface area measurements (Brunauer-Emmett-Teller method), UV/Vis diffuse reflectance spectroscopy, time-resolved fluorescence decay spectroscopy, electron paramagnetic resonance spectroscopy, and photoelectrochemical measurements, were adopted to analyze the structures and physicochemical properties of the as-prpared samples. The results show that the nanoporous bulk g-C3N4 with a particle size of ca. 20 m exhibits a high specific surface area, which is ca. 30.9 times higher than that of the original material. The g-C3N4 with such a structure exhibits an improved adsorption capacity for the target pollutants and is readily separable from the photocatalysis reaction system. It is believed that a two-step protonation process plays a key role in the formation of the structure. Furthermore, this 3D nanoporous bulk g-C3N4 also shows more-efficient photogenerated carrier transfer and separation. As a result, the visible-light photocatalytic activity of g-C3N4 is significantly enhanced, and the degradation rates of methyl orange (MO) and rhodamine B (RhB) dyes over the nanoporous bulk g-C3N4 are ca. 5.0 and 22.3 times higher, respectively, than that over the original material.
Thermal reflux to synthesise C3N4 nanostructures with high yield and enhanced photocatalytic activity in hydrogen evolution

Yihang He,Mingliang Wu,Kunquan Hong

DOI: https://doi.org/10.1039/d4cc01511h

IF: 4.9

2024-06-16

Chemical Communications

Abstract:Graphitic carbon nitride (g-C 3 N 4 ) is an attractive photocatalyst and a thermal reflux method was used to significantly increase the yield of g-C 3 N 4 nanostructures and enhance their photocatalytic activity for H 2 production. When raw material was placed in an inclined quartz tube with the bottom in the high temperature zone and the top in the low temperature zone, the vapor of the raw material was condensed from the top and refluxed to the bottom to then participate in the reaction again. This method can significantly improve the yield of g-C 3 N 4 with an increase of 28.2%. When used as the photocatalyst in water splitting, these g-C 3 N 4 nanostructures exhibit excellent activity with an H 2 production of 2102 μmol h −1 g −1 under visible irradiation, which is 43.2% higher than the sample prepared by a traditional thermal polymerization method. This method is also promising to use for the synthesis of similar two-dimensional nanostructures for effective H 2 production.

chemistry, multidisciplinary
High temperature promoted synthesis of graphitic carbon nitride with porous structure and enhanced photocatalytic activity

Lei Shi,Tao Liang,Lin Liang,Fangxiao Wang,Mengshuai Liu,Jianmin Sun

DOI: https://doi.org/10.1007/s10934-015-0018-6

2015-01-01

Journal of Porous Materials

Abstract:Graphitic carbon nitride (g-C 3 N 4 ) was prepared by the polycondensation of melamine at 650 °C for 2 h, then thoroughly characterized by X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, elemental analysis, transmission electron microscopy, N 2 adsorption–desorption isotherms, UV–Vis diffuse reflectance spectra and photoluminescence spectra. The photocatalytic activity of g-C 3 N 4 catalyst was evaluated by the degradation of Rhodamine B, Methylene blue and phenol solution under visible-light irradiation, which showed that g-C 3 N 4 calcined at 650 °C increased the degree of condensation, thus led to the decreased band gap and exhibited better photocatalytic activity than the reference sample treated at 520 °C and P25. The integrated positive effects of porous structure, larger surface area, stronger visible-light absorption and higher separation efficiency for photoinduced electron–hole pairs over g-C 3 N 4 treated at 650 °C resulted in its improved photocatalytic activity for degrading pollutants. Additionally, the as-prepared g-C 3 N 4 possessed good structural and catalytic stability after three recycles.
Multiple Ordered Porous Honeycombed g-C3N4 with Carbon Ring In-Plane Splicing for Outstanding Photocatalytic H2 Production

Xiaobo Wu,Huiqing Fan,Weijia Wang,Lin Lei,Xinye Chang,Longtao Ma

DOI: https://doi.org/10.1039/d2ta04163d

IF: 11.9

2022-08-08

Journal of Materials Chemistry A

Abstract:Morphology regulation and electronic structure modulation are very important means to improve the photocatalytic H2 evolution of metal-free graphitic carbon nitride (g-C3N4) photocatalyst. Herein, we constructed a multiple ordered porous honeycombed structure of g-C3N4 via one-step chemical vapor deposition (CVD) method with co-pyrolysis of melamine and glucose, in which the carbon ring (Cr) in-plane seamless splicing into g-C3N4 lattice network (denoted as Cr-PHCN). The as-prepared Cr-PHCN exhibits periodically honeycombed structure with ~ 300 nm in inner diameter and ~ 20 nm in wall thickness. The multi-dimensional honeycombed architecture concomitant advantages of enhanced light harvesting ability, abundant active sites and shorter electron transport paths. Simultaneously, in-plane seamless splicing triazine@Cr extends π-conjugated systems, which contributes to narrow band gap, improve electrical conductivity and prohibit electron-hole recombination rate. Accordingly, the average hydrogen evolution rate (HER) of Cr-PHCN reaches 7581 μmol·h-1·g-1, around 47.4 times than that of pure CN (160 μmol·h-1·g-1), and the remarkable apparent quantum efficiency (AQE) attains to 10.62 % at 420 nm. This work successfully achieved the simultaneous morphology control and in-plane modification of high-performance g-C3N4 with high yield.

materials science, multidisciplinary,chemistry, physical,energy & fuels
Microstructure Regulation of Graphitic Carbon Nitride Nanotubes via Quick Thermal Polymerization Process for Photocatalytic Hydrogen Evolution

Jinyu Gao,Mingxia Li,Hui Chen,Liping Guo,Zhenzi Li,Xuepeng Wang

DOI: https://doi.org/10.1016/j.jphotochem.2023.114747

2023-04-03

Abstract:Among multitudinous photocatalytic materials, graphite carbonitride (g-C 3 N 4 ) has been widely explored as a new photocatalyst. The g-C 3 N 4 nanotubes with hollow one-dimensional structure can promote carrier migration along the one-dimensional direction, thereby improving the electron-hole separation efficiency, which has always been a hot spot. However, the collapse of nanotubes in long-term thermal polymerization process leads to the decline of photocatalytic performance, which is expected to be further optimized. Herein, we report g-C 3 N 4 nanotubes (TCN) through short time thermal polymerization to ensure the integrity of g-C 3 N 4 skeleton. And the influence of thermal temperature on the internal formation mechanism of nanotube morphology is investigated. Combined with the unique hollow tube structure and complete framework, the migration of photogenerated carriers is significantly accelerated and the photocatalytic hydrogen evolution performance is improved more than 7 times compared with the original g-C 3 N 4 . This work provides novel insights into the preparation of g-C 3 N 4 nanotubes for photocatalytic applications.

chemistry, physical
Gas bubbling exfoliation strategy towards 3D g-C3N4 hierarchical architecture for superior photocatalytic H2 evolution

Hamza Majeed Ansari,Weijia Wang,Lin Lei,Kuo Bao,Xinye Chang,Ali Raza,Yongfeng Chen,Asad Mehboob,Qi Zhong,Anurag Srivastava,Olga Kaimieva,Huiqing Fan

DOI: https://doi.org/10.1016/j.jallcom.2022.165794

IF: 6.2

2022-10-25

Journal of Alloys and Compounds

Abstract:Graphitic carbon nitride (g-C3N4) shows a graphite-like layered structure, which provides a high theoretical value for solar-to-hydrogen evolution especially for a 2D nanostructure. However, conventional polycondensation induces a strong agglomeration and collapse of nanostructure, resulting in a relatively poor photocatalytic performance. To overcome this problem, we develop a gas bubbling exfoliation strategy with NH4Cl assistant to make ultrathin 2D g-C3N4 nanosheets self-assembled into a 3D macroporous network on a large scale. The hierarchical structure significantly improves the specific surface area to 176.4 m2 g−1 (11.6 times higher than the reference g-C3N4), which allows a large water/g-C3N4 interface for photocatalytic water reduction reaction. The ultrathin 2D g-C3N4 nanosheets show a thickness of about 1.4 nm, which greatly suppress photoinduced carriers recombination and enhance charge transfer at the interface. Furthermore, the doping of N and Cl is achieved during synthesis. As a result, the resulting g-C3N4 demonstrates a remarkable improvement in H2 production of 12.89 mmol g-1 h−1, which is 21 times higher than the g-C3N4 obtained from the conventional condensation method. These explorations provide a facile guidance for the quasi 3D g-C3N4 hierarchical architecture engineering even for various energy-related applications.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

A "Ship-in-a-bottle" Strategy to Fabricate Highly Crystallized Nanoporous Graphitic C3N4 Microspheres under Pressurized Conditions

Highly crystalline carbon nitride hollow spheres with enhanced photocatalytic performance

One-pot synthesis of porous g-C3N4 nanosheets with enhanced photocatalytic activity under visible light

Template-free Preparation and Characterization of Nanoporous G-C3n4 with Enhanced Visible Photocatalytic Activity

"Alternated Cooling and Heating" Strategy Enables Rapid Fabrication of Highly-Crystalline G-C3n4 Nanosheets for Efficient Photocatalytic Water Purification under Visible Light Irradiation

Moderate NaNO2 Etching Enables Easy Crystallinity Optimization of G-C3n4 with Superior Photoreduction Performance

Supermolecule Polymer Derived Porous Carbon Nitride Microspheres with Controllable Energy Band Structure for Photocatalytic Hydrogen Evolution Reaction

Electrostatic self-assembly combined with microwave hydrothermal strategy: construction of 1D/1D carbon nanofibers/crystalline g-C3N4 heterojunction for boosting photocatalytic hydrogen production

Nanoporous Graphitic Carbon Nitride With Enhanced Photocatalytic Performance

“Carbon Diffusion” Engineered Carbon Nitride Nanosheets for High-Efficiency Photocatalytic Solar-to-fuels Conversion

2D Porous N-Deficient G-C3n4 Nanosheet Decorated with CdS Nanoparticles for Enhanced Visible-Light-Driven Photocatalysis

A Template Induced Method to Synthesize Nanoporous Graphitic Carbon Nitride with Enhanced Photocatalytic Activity under Visible Light

Synthesis of g-C3N4 from Various Precursors for Photocatalytic H2 Evolution under the Visible Light

Facile Urea-Assisted Precursor Pre-Treatment to Fabricate Porous G-C3n4 Nanosheets for Remarkably Enhanced Visible-Light-driven Hydrogen Evolution

Self-assembled B-doped flower-like graphitic carbon nitride with high specific surface area for enhanced photocatalytic performance

Template‐Free Synthesis of Three‐Dimensional Nanoporous Bulk Graphitic Carbon Nitride with Remarkably Enhanced Photocatalytic Activity and Good Separation Properties

Thermal reflux to synthesise C3N4 nanostructures with high yield and enhanced photocatalytic activity in hydrogen evolution

High temperature promoted synthesis of graphitic carbon nitride with porous structure and enhanced photocatalytic activity

Multiple Ordered Porous Honeycombed g-C3N4 with Carbon Ring In-Plane Splicing for Outstanding Photocatalytic H2 Production

Microstructure Regulation of Graphitic Carbon Nitride Nanotubes via Quick Thermal Polymerization Process for Photocatalytic Hydrogen Evolution

Gas bubbling exfoliation strategy towards 3D g-C3N4 hierarchical architecture for superior photocatalytic H2 evolution