Carbon Nanolayer-Wrapped Mesoporous TiO 2 –B/Anatase for Li + Storage
Yan Wang,Simeng Yao,Cuiping Yu,Jianfang Zhang,Jiewu Cui,Yongqiang Qin,Hongmei Zheng,Yong Zhang,Jingjie Wu,Yucheng Wu
DOI: https://doi.org/10.1021/acsanm.1c01154
IF: 6.14
2021-07-20
ACS Applied Nano Materials
Abstract:Optimizing the microstructure, the chemical composition, the surface-wrapped carbon nanolayer, and oxygen vacancies is expected to be an effective strategy for ameliorating electrochemical performance of anode materials. In this work, a series of mesoporous TiO<sub>2</sub> with different phase compositions and carbon nanolayers have been rationally designed and constructed. The <i>in situ</i>-synthesized carbon nanolayer could not only lead to the enhanced electric conductivity but also promote the content and stability of TiO<sub>2</sub>–B in the TiO<sub>2</sub>–B/anatase mixed phases. Moreover, mesoporous TiO<sub>2</sub> composites consisting of different ratios of TiO<sub>2</sub>–B/anatase with desired interfaces can be obtained by tailoring the carbonization temperature. As a result, the carbon nanolayer-coated mesoporous TiO<sub>2</sub> with the dual phase obtained at 600 °C (TiO<sub>2</sub>–B/) not only achieves a high specific capacity (473.5 mA h g<sup>–1</sup> at 0.1 A g<sup>–1</sup>) and a superior rate performance (181.9 mA h g<sup>–1</sup> at a high current density of 5 A g<sup>–1</sup>) but also displays a long cycling lifetime by retaining 134% of its initial capacity after 1000 cycles at 1.0 A g<sup>–1</sup>. The boosted electrochemical properties are owing to synergistic effects of the unique dual phase (TiO<sub>2</sub>–B/anatase) with an optimized mass ratio, the rich defects in the anatase/TiO<sub>2</sub>–B interface, the mesoporous structure, and the surface-wrapped highly conductive carbon layer. This work demonstrates an innovative approach to construct mesoporous TiO<sub>2</sub> nanocomposites with superior Li<sup>+</sup> storage performance.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsanm.1c01154?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsanm.1c01154</a>.XRD patterns; Raman spectra of TiO2-B/; TGA curve of TiO2-B/; TEM images and EDS mapping; HRTEM images; nitrogen adsorption-desorption isotherms; XPS spectra; cyclic voltammetry curves; Nyquist plots; impedance parameters of TiO2-B/ and TiO2-B/anatase-6; linear fittings; discharge capacity values; rate capability; comparison of rate performance between TiO2-B/ and TiO2/anatase-based and TiO2-based anodes; cycling performance; and SEM image (<a class="ext-link" href="/doi/suppl/10.1021/acsanm.1c01154/suppl_file/an1c01154_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology