Abstract:Carbon Fiber Reinforced Polymer (CFRP) composites are widely used in aircraft structures, because of their superior mechanical and lightweight properties. CFRP composites are often exposed to hygrothermal environments in service. Temperature and moisture can affect the material properties of composites. In order to make clear the moisture diffusion behavior and the properties degradation of composites, the TG800/E207 composite laminates with four stacking sequences [0]16, [90]16, [+/- 45]4s, and [(+45/0/0/-45)s]s are designed and manufactured. Moisture absorption tests are carried out at 80 celcius, 90 %RH. It is shown that the moisture absorption curves of composite laminates present a three-stage. A modified Fickian model was proposed to capture the diffusion behavior of TG800/E207 composite laminates. The relationships among the non-Fickian parameters, the environmental parameters and the stacking sequences of CFRP were correlated and compared. Results showed that the modified Fickian curve is sensitive to the diffusivity of Stage I and Stage II. Compared with unaged specimens, the maximum tensile stress for [0]16, [90]16, [+/- 45]4s, and [(+45/0/0/-45)s]s decreased by 14.94 %, 28.15 %, 11.96 %, and 26.36 %, respectively. The strains at failure for [0]16, [90]16, [+/- 45]4s, and [(+45/0/0/-45)s]s decreased by 55.38 %, 62.65 %, 46.41 %, and 31.71 %, respectively. The elastic modulus for [0]16, [90]16, [+/- 45]4s, and [(+45/0/0/-45)s]s increased by 90.93 %, 94.57 %, 49.22 %, and 8.22 %, respectively. [90]16 sample has the minimum saturated moisture content and the maximum strength degeneration.(c) 2022 Chinese Society of Aeronautics and Astronautics. Production and hosting by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Water Diffusion in Carbon Fiber Reinforced Polyamide 6 Composites: Experimental, Theoretical, and Numerical Approaches

Experimental Investigation of Moisture Diffusion in Short‐glass‐fiber‐reinforced Polyamide 6,6

Numerical Modeling of Moisture Diffusion in an Unidirectional Fiber‐reinforced Polymer Composite

Experimental and Numerical Study on Moisture Diffusion Behavior of 3D Woven Composite

Visual Experiments for Water Absorbing Process of Fiber-Reinforced Composites

Effects of Hydrothermal Aging on Moisture Absorption and Property Prediction of Short Carbon Fiber Reinforced Polyamide 6 Composites

Influence of hydrothermal environment on mechanical behavior of fiber reinforced polymers: characterization and modeling

Moisture Diffusion Characterization of Carbon Fiber Based Polymeric Composites under Recurrent Hygrothermal Ageing

Hygrothermal aging effect on the water diffusion in glass fiber reinforced polymer (GFRP) composite: Experimental study and numerical simulation

Numerical Simulation of Non-Fick Moisture Diffusion of Pultruded Composite GFRP Bridge Deck Plates

Dimensional Stability And Mechanical Performance Evolution Of Continuous Carbon Fiber Reinforced Polyamide 6 Composites Under Hygrothermal Environment

Moisture Diffusion and Damage Characteristics of Carbon Fabric Reinforced Polyamide 6 Laminates under Hydrothermal Aging

Research on Water-Sorption Behaviors of T700/9916 Composite Laminates

Diffusion of water in glass fiber reinforced polymer composites at different temperatures

Effect of hygrothermal aging on moisture diffusion and tensile behavior of CFRP composite laminates

The Two Stage Moisture Diffusion Model for Non-Fickian Behaviors of 3D Woven Composite Exposed Based on Time Fractional Diffusion Equation

Numerical Simulation of Moisture Diffusion in Pultruded GFRP Composite Profile

Hygrothermal Behavior of Carbon Fiber Fabric Reinforced Vinylester Resin Composite Structures

Simulation of Fiber Reinforced Composite Materials Mold Filling Process and Mechanical Properties Analysis

Mechanical Performance of Carbon Fiber/Polyamide 6: Comparative Study Between Conditioning in Distilled Water with Heating and Saline Solution

Moisture Absorption Characterization of Carbon Fiber‐reinforced Polymer Using Fickian and Non‐fickian Models