Wide-range thermometry and up-conversion luminescence of Ca 5 (PO 4 ) 3 F:Yb 3+ /Er 3+ transparent glass ceramics

Xiangyu Liu,Yong Chen,Fei Shang,Guohua Chen,Jiwen Xu

DOI: https://doi.org/10.1007/s10854-019-00865-5

2019-01-01

Abstract:Ca 5 (PO 4 ) 3 F:Yb 3+ /Er 3+ glass ceramics (GCs) were successfully manufactured via traditional controlled crystallization method. The structural, optical and up-conversion (UC) illuminant properties were systemically investigated by XRD, TEM, HRTEM, fluorescence spectra and luminescence lifetime measurements. The results show that Ca 5 (PO 4 ) 3 F:Yb 3+ /Er 3+ nanocrystals has been precipitated from the precursor glass matrix and the UC luminescence mechanism of PG and GC660 is two-photon process. The enhanced UC emission intensity and extended lifetime of Er 3+ is observed in the GCs. Using the temperature dependent fluorescence intensity ratio (FIR) of thermally coupled emitting states ( 4 S 3/2 , 2 H 11/2 ) as thermometric index, Ca 5 (PO 4 ) 3 F:Yb 3+ /Er 3+ GCs present wide temperature-sensing range (298–798 K) and high absolute sensitivity (51.9 × 10 −4 K −1 at 600 K). This finding suggests that Ca 5 (PO 4 ) 3 F:Yb 3+ /Er 3+ GC materials are promising in optical temperature measurement field.