Abstract:Sensitive H-2 gas sensors are highly desirable for the prediction and early-warning of H-2 leakage. Low-dimensional nanostructures of metal oxide semiconductor emerge as promising materials candidates, but it remains a challenge to preserve the nanostructures in the real sensors. In this work, we demonstrated highly sensitive H-2 gas sensors based on porous network of SnO2 nanowires that exhibited ultrasmall diameter similar to 2 nm. Colloidal SnO2 nanowires synthesized via a solvothermal process were drop-coated onto the commercial alumina substrates, followed by in-situ annealing treatment at 350 degrees C to remove the surface ligands. The sensors exhibited sensitive response with linear dependence on the H-2 gas concentration ranging from 2 ppm to 100 ppm when operated at 250 degrees C. Typically, the sensor had a response of 13 toward 40 ppm of H-2, with the response and recovery time being 15 s and 31 s, respectively. To further improve the sensor performance, Palladium doped SnO2 nanowires were thoroughly investigated. It's shown that, the operating temperature of the sensor decreased from 250 degrees C to 150 degrees C after Pd doping, and the response and recovery time decreased to 6 s/3 s. The superb sensitivity was attributed to the enhanced gas reception, electron transport as well as utility factor owing to the network nanostructure of ultrathin SnO2 nanowires and catalytic activity of Pd, according to theoretical calculation and adsorption kinetics studies. Combined with the excellent solution processability, the colloidal SnO2 nanowires are potentially attractive for next-generation gas sensors with lower power consumption and integration with silicon-based substrates.

Pd-Loaded Sno2 Hierarchical Nanospheres For A High Dynamic Range H2s Micro Sensor

Sensitive H2 Gas Sensors Based on SnO2 Nanowires

Microwave Assisted Synthesis of Hierarchical Pd/Sno2 Nanostructures for Co Gas Sensor

Ultrasensitive hydrogen sensor based on Pd0-Loaded SnO 2 electrospun nanofibers at room temperature

Ultrasensitive Gas Sensor Based on Pd/SnS2/SnO2 Nanocomposites for Rapid Detection of H2

Ordered mesoporous Pd/SnO2 synthesized by a nanocasting route for high hydrogen sensing performance

Pd nanoparticles composited SnO2 microspheres as sensing materials for gas sensors with enhanced hydrogen response performances

Pd nanoparticles decorated SnO 2 ultrathin nanosheets for highly sensitive H 2 sensor: Experimental and theoretical studies

Preparation of Pd/PdO Loaded WO3 Microspheres for H2S Detection

Pd-Loaded Sno2 Ultrathin Nanorod-Assembled Hollow Microspheres with the Significant Improvement for Toluene Detection

One-step Synthesis and Gas Sensing Properties of Hierarchical Cd-doped SnO2 Nanostructures

Hydrogen Gas Sensor Based on SnO2 Nanospheres Modified with Sb2O3 Prepared by One-Step Solvothermal Route

Synergistic Effect of PdO and Parallel Nanowires Assembled CuO Microspheres Enables High Performance Room-Temperature H2S Sensor

Development of Sensors Based on CuO-doped SnO2 Hollow Spheres for Ppb Level H2S Gas Sensing

Pt Nanoparticle-Modified SnO<sub>2</sub>-ZnO Core-Shell Nanosheets on Microelectromechanical Systems for Enhanced H<sub>2</sub>S Detection

Nano-Schottky Junction-Engineered Pd/SnO2 Nanotube Array for Ultrasensitive Hydrogen Sensing at Room Temperature

Ultrafine Nanoparticles of W-doped SnO2 for Durable H2S Sensors with Fast Response and Recovery.

Co-PBA MOF-derived Hierarchical Hollow Co3O4@NiO Microcubes Functionalized with Pt for Superior H2S Sensing

Pt Nanoparticle-Modified SnO 2 –ZnO Core–Shell Nanosheets on Microelectromechanical Systems for Enhanced H 2 S Detection

The enhanced CO gas sensing performance of Pd/SnO2 hollow sphere sensors under hydrothermal conditions

Enhancement of Hydrogen Monitoring Properties Based on Pd–SnO2 Composite Nanofibers