Zr and Gd Co-Doped Ceria Oxide Conductor with Low Electronic Conductivity in Reducing Atmosphere
Wei-Xin Yan,Zhi-Lin Ji,Dong-Yun Gui,Fa Luo,Dong-Mei Zhu,Chun-Hai Wang
DOI: https://doi.org/10.1016/j.ceramint.2024.07.061
IF: 5.532
2024-01-01
Ceramics International
Abstract:The Gd and Zr co-doped ceria electrolyte Gd0.1Ce0.9-xZrxO1.95 (x = 0, 0.03, 0.06, 0.09, 0.12, 0.15, labeled as GDC, Zr0.03GDC, Zr0.06GDC, Zr0.09GDC, Zr0.12GDC, Zr0.15GDC) was synthesized by solid-state reaction. The XRD and Rietveld refinements reveal that ZrxGDC is in a cubic fluorite phase with the cell parameters a decrease from 5.4186(1) to 5.3728(1) & Aring; and cell volume V decreases 159.10(2) to 155.09(2) & Aring;(3) as the x increases from 0 to 0.15. SEM studies confirm a dense microstructure with well-defined grains in a size of 10-20 mu m. The Raman spectra agree with the fact that a solid solution is formed and the blue-shift of Raman modes is observed as expected. XPS analysis shows that Ce4+ is more stable in Zr doped GDC. The conductivity of Zr0.03GDC reaches 1.2 x 10(-3) S/cm at 450 degrees C. The bond valence of Ce4+ is constrained to a higher one as the Ce4+ is substituted by Zr4+ in the solid solution, and a higher stability in the reducing atmosphere was achieved. The electronic conductivity decreases from 14.8% of GDC to 0.1% of Zr0.03GDC at 400 degrees C. The oxygen ion transference number of Zr0.03GDC is improved significantly to > 0.93 in 3% H-2/Ar at 700 degrees C.