Vertically Aligned and Ordered Arrays of 2D MCo 2 S 4 @Metal with Ultrafast Ion/Electron Transport for Thickness-Independent Pseudocapacitive Energy Storage
Zongbin Hao,Xingchen He,Hongdou Li,Denis Trefilov,Yangyang Song,Yang Li,Xinxin Fu,Yushuang Cui,Shaochun Tang,Haixiong Ge,Yanfeng Chen
DOI: https://doi.org/10.1021/acsnano.0c02973
IF: 17.1
2020-09-16
ACS Nano
Abstract:Pseudocapacitance holds great promise for energy density improvement of supercapacitors, but electrode materials show practical capacity far below theoretical values due to limited ion diffusion accessibility and/or low electron transferability. Herein, inducing two kinds of straight ion-movement channels and fast charge storage/delivery for enhanced reaction kinetics is proposed. Very thick electrodes consisting of vertically aligned and ordered arrays of NiCo<sub>2</sub>S<sub>4</sub>-nanoflake-covered slender nickel columns (NCs) are achieved <i>via</i> a scalable route. The vertical standing ∼5 nm ultrathin NiCo<sub>2</sub>S<sub>4</sub> flakes build a porous covering with straight ion channels without the "dead volume", leading to thickness-independent capacity. Benefiting from the architecture acting as a "superhighway" for ultrafast ion/electron transport and providing a large surface area, high electrical conductivity, and abundant availability of electrochemical active sites, the NiCo<sub>2</sub>S<sub>4</sub>@NC-array electrode achieves a specific capacity up to 486.9 mAh g<sup>–1</sup>. The electrode even can work with a high specific capacity of 150 mAh g<sup>–1</sup> at a very high current density of 100 A g<sup>–1</sup>. In particular, due to the advanced structure features, the electrode exhibits excellent flexibility with a unexpected improvement of capacity when being largely bent and excellent cycling stability with an obvious resistance decrease after the cycles. An asymmetric pseudocapacitor applying the NiCo<sub>2</sub>S<sub>4</sub>@NC-array as a positive electrode achieves an energy density of 66.5 Wh kg<sup>–1</sup> at a power density of 400 W kg<sup>–1</sup>, superior to the most reported values for asymmetric devices with NiCo<sub>2</sub>S<sub>4</sub> electrodes. This work provides a scalable approach with mold-replication-like simplicity toward achieving thickness-independent electrodes with ultrafast ion/electron transport for energy storage.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.0c02973?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.0c02973</a>.Illustration of synthesis process of a nickel template; XRD patterns of the typical NiCo<sub>2</sub>S<sub>4</sub>@NC-array and the bare NC-array; physicochemical characterization results of the NiCo<sub>2</sub>S<sub>4</sub>@NC-array electrode including the XPS spectra and SEM images; SEM images of FeCo<sub>2</sub>S<sub>4</sub> nanowires at NC-array; CV and GCD curves of the NiCo<sub>2</sub>S<sub>4</sub>@NC-array electrodes obtained with different <i>t</i><sub>R</sub>; low-magnification SEM-EDS elemental mappings and XPS analysis of the NiCo<sub>2</sub>S<sub>4</sub>@NC-array electrode after 2000 cycles; SEM image of a porous pressed on a Ni foam and CV curves of the positive and negative electrodes recorded at 20 mV s<sup>–1</sup>; table presenting the electrochemical performance comparison with other reported values (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.0c02973/suppl_file/nn0c02973_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology