A novel red phosphor Cs2NaGaF6:Mn4+ with ultra-strong zero-phonon lines and long wavelength phonon sidebands for high-quality WLEDs
Zhijian Liao,Yan Li,Jiaxing Zuo,Guang Chen,Shihao Wu,Jiaqing Peng,Xinyu Ye,Wanfang Zou
DOI: https://doi.org/10.1039/d2dt03890k
IF: 4
2023-02-08
Dalton Transactions
Abstract:For high-efficiency lighting and wide color gamut backlight display, high-quality narrow-band red phosphor for WLEDs is still in urgent demand. Herein, a novel red-emitting fluoride phosphor Cs2NaGaF6:Mn4+ was successfully synthesized by a simple two-step co-precipitation method, which exhibits ultra-intense zero-phonon line (ZPL) and two sets of vibrational phonon sidebands under 468 nm blue light irradiation. The ZPL emission peak of Cs2NaGaF6:Mn4+ locates at 627 nm, which is much stronger than its υ6 vibration peak, more matchable with the eye-sensitive region of humans, and beneficial to obtain higher luminous efficiency of WLEDs. Interestingly, the υ6 vibration peak of this red phosphor is at 636.5 nm, which exhibits a red-shift of about 6.5 nm compared to the common fluoride phosphor of A2BF6:Mn4+ (usually at about 630 nm, represented by K2SiF6:Mn4+). Thanks to the longer wavelength of υ6 vibration peak, chromaticity coordinates of (0.7026, 0.2910) with a larger x-coordinate value were realized, leading to a potentially wider color gamut of WLEDs. In addition, this phosphor has high thermal stability, and its emission intensity at 423 K remains 93.7% of the initial intensity at room temperature. The lumen efficiency of WLED1 combined a mixture of Cs2NaGaF6:Mn4+ and YAG:Ce3+ with InGaN blue chip is 115.73 lm·W-1 with Tc=3390 K and Ra=92.5under a 20 mA driving current. The chromaticity coordinates of WLED2 packaged Cs2NaGaF6:Mn4+ with β-SiAlON:Eu2+ and InGaN blue chip are (0.3149,0.3262), and the calculated color gamut is up to 118.4% (NTSC). These results indicate that Cs2NaGaF6:Mn4+ red phosphors have a promising application in high-quality lighting and display fields.
chemistry, inorganic & nuclear