Effect of crystalline transformation on supercritical CO 2 foaming and cell morphology of isotactic polybutene-1
Weijie Li,Zheng Gong,Kaiwen Wu,Ling Zhao,Dongdong Hu
DOI: https://doi.org/10.1016/j.jcou.2023.102546
IF: 7.7
2023-07-20
Journal of CO2 Utilization
Abstract:As a polycrystalline polymer, isotactic polybutene-1 (iPB-1) will form different crystalline structures when it crystallizes under different conditions. In this work, we found a simple method to manipulate the cell structure of iPB-1 foams by controlling the annealing time of crystalline form II at room temperature and employing supercritical CO 2 foaming. As the content of crystalline form II increases, the storage modulus (G′) and complex viscosity (|η * |) increase, and the solubility of CO 2 in iPB-1 increases. Crystalline form II has a wider foaming temperature window compared to crystalline form I and exhibits a more uniform cell structure at temperatures between 95 °C and 125 °C. The average cell diameters of crystalline form II and I are 33.9 μm and 11.2 μm at 115 °C and 15 MPa CO 2 , respectively. A small amount of crystalline form I acts as a heterogeneous nucleation agent during the foaming process, resulting in the formation of a "petal-like" cell structure. During the foaming saturation process, the melted portion of iPB-1 with unstable crystalline form II transforms into crystalline form I′ under high-pressure CO 2 , while the unmelted portion transforms into crystalline form I. As the pressure increases, the cell structure of iPB-1 undergoes a transition from "petal-like" to bimodal cell structure, ultimately achieving a more uniform structure. Moreover, increasing foaming pressure can also change the cell structure of the foamed material from closed-cell to open-cell. The occurrence of bimodal melting peaks in the foamed samples is beneficial for the adhesion of beads during the molding process.
engineering, chemical,chemistry, multidisciplinary