PdAg bimetallic electrocatalyst for highly selective reduction of CO2 with low COOH* formation energy and facile CO desorption
Rui Lin,Xuelu Ma,Weng-Chon Cheong,Chao Zhang,Wei Zhu,Jiajing Pei,Kaiyue Zhang,Bin Wang,Shiyou Liang,Yuxi Liu,Zhongbin Zhuang,Rong Yu,Hai Xiao,Jun Li,Dingsheng Wang,Qing Peng,Chen Chen,Yadong Li
DOI: https://doi.org/10.1007/s12274-019-2526-1
IF: 9.9
2019-10-17
Nano Research
Abstract:For electrocatalytic reduction of CO2 to CO, the stabilization of intermediate COOH* and the desorption of CO* are two key steps. Pd can easily stabilize COOH*, whereas the strong CO* binding to Pd surface results in severe poisoning, thus lowering catalytic activity and stability for CO2 reduction. On Ag surface, CO* desorbs readily, while COOH* requires a relatively high formation energy, leading to a high overpotential. In light of the above issues, we successfully designed the PdAg bimetallic catalyst to circumvent the drawbacks of sole Pd and Ag. The PdAg catalyst with Ag-terminated surface not only shows a much lower overpotential (-0.55 V with CO current density of 1 mA/cm2) than Ag (−0.76 V), but also delivers a CO/H2 ratio 18 times as high as that for Pd at the potential of -0.75 V vs. RHE. The issue of CO poisoning is significantly alleviated on Ag-terminated PdAg surface, with the stability well retained after 4 h electrolysis at -0.75 V vs. RHE. Density functional theory (DFT) calculations reveal that the Ag-terminated PdAg surface features a lowered formation energy for COOH* and weakened adsorption for CO*, which both contribute to the enhanced performance for CO2 reduction.
materials science, multidisciplinary,chemistry, physical,physics, applied,nanoscience & nanotechnology