Abstract:Molybdenum sulfide (MoS2) is considered as low-cost catalyst with great potential for hydrogen evolution reaction (HER). In this contribution, a promising Mo-precursor was first designed and prepared via partial reduction of commercial (NH4)(6)Mo7O24 center dot 4H(2)O by DL-tartaric acid. A simple pyrolysis method as a new "bottom-up" approach was then developed to achieve the desired HER catalysts by using the Mo-precursor. The resulting catalysts consist of multiphasic 1T/2H-MoS2 and residual S, N co-doped carbon (SNC) with oxygen functional groups. In comparison with (NH4)(6)Mo7O24 center dot 4H(2)O, Mo-precursor with high content of Mo5+ promotes the full formation of MoS2, while its high content of carbon is more favorable to gain the residual SNC in the resulting catalysts. The further results demonstrate that the percentages of 1T-MoS2 and the content of the residual SNC can be facilely tuned by the pyrolysis temperatures or the Mo/S feeding molar ratios. Notably, although the resulting catalysts exhibit the "bulk" and irregular morphology with low specific surface areas, the high percentages of 1T-MoS2 as the primary advantage, the highly exposed active sites mainly stemming from disordered stacking of S-Mo-S layers, and the high content of the SNC residues are synergistically responsible for their high electrocatalytic HER activity. The high thermal stability of 1T-MoS2 and the excellent durability and stability during HER processes are attributed to the stabilizing effects of the residual SNC. Under the optimized synthetic conditions, the achieved Mo/S(0.2)-450 has a low overpotential of similar to 130 mV at 10 mA cm(-2), a low Tafel slope of 77 mV dec(-1), a high specific activity of 17.53 mu A cm(Cat center dot)(-2), and the excellent durability and stability in 0.5 M H2SO4. This work can provide a promising Mo-precursor and a facile route to developing the highly efficient HER catalysts.

MoS2 In-Situ Growth on Melamine Foam for Hydrogen Evolution

MoS2/graphene/carbonized melamine foam composite catalysts for the hydrogen evolution reaction

Confined Growth of MoS2 by using a Two‐Dimensional Metal‐Organic Framework for Efficient Hydrogen Evolution

Design of Dual-Modified MoS2 with Nanoporous Ni and Graphene as Efficient Catalysts for the Hydrogen Evolution Reaction

MoS2 formed on mesoporous graphene as a highly active catalyst for hydrogen evolution

Space-Confined Growth of Mos2 Nanosheets Within Graphite: the Layered Hybrid of Mos2 and Graphene As an Active Catalyst for Hydrogen Evolution Reaction

Ultrathin Mos2 Nanosheets Growing Within an In-Situ-Formed Template As Efficient Electrocatalysts for Hydrogen Evolution

Epitaxial MoS2 Nanosheets on Nitrogen Doped Graphite Foam As a 3D Electrode for Highly Efficient Electrochemical Hydrogen Evolution

MoS2 Supported CoS2 on Carbon Cloth As a High-Performance Electrode for Hydrogen Evolution Reaction

Crystalline MoP-amorphous MoS2 hybrid for superior hydrogen evolution reaction

MoS 2 /CoS 2 with heterostructure in-situ grown on the surface of electrospinning carbon nanotube for efficient hydrogen evolution reaction

Structural Aspects of MoS x Prepared by Atomic Layer Deposition for Hydrogen Evolution Reaction

Mos2/Cos2 with Heterostructure In-Situ Grown on the Surface of Electrospinning Carbon Nanotube for Efficient Hydrogen Evolution Reaction

Synthesis, Characterization, and Hydrogen Evolution Reaction Activity of MoS2 Nanostructures Prepared Using Nonionic Surfactant

Boosting hydrogen evolution on MoS2 via co-confining selenium in surface and cobalt in inner layer

“Bulk” 1T/2h-Mos2 with Tunable Phases and Residual S, N Co-Doped Carbon As a Highly Active and Durable Catalyst for Hydrogen Evolution

Rational Design of Freestanding MoS2 Monolayers for Hydrogen Evolution Reaction

Molten salt electrolysis method to achieve Ni/MoS2 with activity sulfur enhance the hydrogen evolution reaction performance under alkaline condition

MoS2-CuCo2S4 nanosheets with a honeycomb structure formed on Ni foam: An efficient electrocatalyst for hydrogen evolution reaction

Growth of MoS2 nanosheets on M@N-doped carbon particles (M = Co, Fe or CoFe Alloy) as an efficient electrocatalyst toward hydrogen evolution reaction

Heterostructure Engineering of MoS2/Mo2CTx Nanoarray Via Molten Salt Synthesis for Enhanced Hydrogen Evolution Reaction