Abstract:A small molecule [2‐(9‐H‐Carbazol‐9‐yl) ethyl] phosphonic acid (2PACz) is introduced into low donor and acceptor ratio (1:3) semitransparent organic solar cells. Due to the mitigated charge recombination and strengthened charge extraction, a remarkable efficiency of 15.2% is achieved with an average visible transmittance (AVT) of 19.2%, which represents the highest efficiency in semitransparent devices with AVT around 20%.Semitransparent organic solar cells (ST‐OSCs) have promising prospects for building or vehicle integrated solar energy harvesting with energy generation and see‐through function. How to achieve both an adequate average visible transmittance (AVT) and high‐power conversion efficiency (PCE) is always the key issue. Herein, a simple but effective strategy for constructing high performance ST‐OSCs by introducing a small molecule [2‐(9‐H‐Carbazol‐9‐yl) ethyl] phosphonic acid (2PACz) into a low‐donor content active layer is reported. The fill factor is improved from 70.5% to 75.5% and correlated to the mitigated charge recombination and strengthened charge extraction, further ascribed to the enhanced build‐in potential, reduced charge transport resistance, and favorable film morphology. By combining the unique nature of 2PACz, that can spontaneously form in situ self‐organized hole transport interlayers under bulk‐heterojunction films, PEDOT‐free ST‐OSCs with a PCE of 15.2%, amongst the highest values in this field, is achieved with an AVT of 19.2%. Moreover, an outstanding light utilization efficiency of 3.39% is also obtained with an AVT of 30.0% and a PCE of 11.3% in a translucent device by tuning the electrode. The work demonstrates a new and simple strategy for achieving excellent AVT and PCE in ST‐OSCs with simplified device structure.

Highly-efficient Semi-Transparent Organic Solar Cells Utilising Non-Fullerene Acceptors with Optimised Multilayer MoO3/Ag/MoO3 Electrodes

Light Management for Fullerene-Based Semitransparent Polymer Solar Cells with a Distributed Bragg Reflector

Efficiency and average visible light transmittance improved simultaneously of the semitransparent organic solar cells

Semitransparent Polymer-Based Solar Cells with Aluminum-Doped Zinc Oxide Electrodes

Semitransparent Flexible Organic Solar Cells

Towards High-Efficiency Non-Fullerene Organic Solar Cells: Matching Small Molecule/polymer Donor/acceptor

The role of structural parameters on efficiency and transparency of semi-transparent non-fullerene organic solar cell

Synergic Interface and Optical Engineering for High‐Performance Semitransparent Polymer Solar Cells

Highly Efficient Polymer Tandem Cells and Semitransparent Cells for Solar Energy

Semitransparent Ternary Nonfullerene Polymer Solar Cells Exhibiting 9.40% Efficiency and 24.6% Average Visible Transmittance

A Nonfullerene Semitransparent Tandem Organic Solar Cell with 10.5% Power Conversion Efficiency

Improving the charge transport of the ternary blend active layer for efficient semitransparent organic solar cells

Highly Efficient Ternary-Blend Polymer Solar Cells Enabled by a Nonfullerene Acceptor and Two Polymer Donors with a Broad Composition Tolerance.

High‐Performance Semitransparent and Bifacial Perovskite Solar Cells with MoO x /Ag/WO x as the Rear Transparent Electrode

Complete Solution-Processed Semitransparent and Flexible Organic Solar Cells: A Success of Polyimide/Ag-Nanowires- and PH1000-Based Electrodes with Plasmonic Enhanced Light Absorption

Ito-Free Semitransparent Organic Solar Cells Based on Silver Thin Film Electrodes

Efficient Top Illuminated Microcavity Organic Solar Cells Using Air Stable Composite Semitransparent Electrodes

Multifunctional Ternary Semitransparent Organic Solar Cell Module with Area above 100 Cm2 and Average Visible Transmittance above 30%

Semitransparent Organic Solar Cells with Efficiency Surpassing 15%

A micro-cavity forming electrode with high thermal stability for semi-transparent colorful organic photovoltaics exceeding 13% power conversion efficiency

Efficient Ternary Organic Solar Cells Enabled by the Integration of Nonfullerene and Fullerene Acceptors with a Broad Composition Tolerance