In Situ Measurements of the Mechanical Properties of Electrochemically Deposited Li 2 CO 3 and Li 2 O Nanorods
Hongjun Ye,Siwei Gui,Zaifa Wang,Jingzhao Chen,Qiunan Liu,Xuedong Zhang,Peng Jia,Yushu Tang,Tingting Yang,Congcong Du,Lin Geng,Hui Li,Qiushi Dai,Yongfu Tang,Liqiang Zhang,Hui Yang,Jianyu Huang
DOI: https://doi.org/10.1021/acsami.1c13732
2021-09-13
Abstract:Solid-electrolyte interface (SEI) is "the most important but least understood (component) in rechargeable Li-ion batteries". The ideal SEI requires high elastic strength and can resist the penetration of a Li dendrite mechanically, which is vital for inhibiting the dendrite growth in lithium batteries. Even though Li2CO3 and Li2O are identified as the major components of SEI, their mechanical properties are not well understood. Herein, SEI-related materials such as Li2CO3 and Li2O were electrochemically deposited using an environmental transmission electron microscopy (ETEM), and their mechanical properties were assessed by in situ atomic force microscopy (AFM) and inverse finite element simulations. Both Li2CO3 and Li2O exhibit nanocrystalline structures and good plasticity. The ultimate strength of Li2CO3 ranges from 192 to 330 MPa, while that of Li2O is less than 100 MPa. These results provide a new understanding of the SEI and its related dendritic problems in lithium batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c13732.TEM images of growth, compression, and tensile tests of the Li2CO3 and Li2O nanorods; the SAED and EELS of the Li2CO3 and Li2O nanorods; the growth rate–time plot of the Li2CO3 and Li2O nanorods; force–deformation data corresponding to the compression of the Li2CO3 and Li2O nanorods; inverse finite element simulation derived stress–strain data for the Li2CO3 and Li2O nanorods (PDF)In situ TEM movie showing the growth of a Li2CO3 nanorod (corresponding to Figure 1). The Li2CO3 grew directly along the CNT. The movie was recorded at 5 frames/s in TEM bright-field images and played at 312× speed (AVI)In situ TEM movie showing the growth of a Li2CO3 nanorod (corresponding to Figure S1). The Li2CO3 grew directly along the CNT. The movie was recorded at 5 frames/s in TEM bright-field images and played at 84× speed (AVI)In situ TEM movie showing the compression of a Li2CO3 nanorod (corresponding to Figure 2). The movie was recorded at 5 frames/s in TEM bright-field images and played at 12× speed (AVI)In situ TEM movie showing the compression experiment of a Li2CO3 nanorod (corresponding to Figure S3). The movie was recorded at 5 frames/s in TEM-bright field images and played at 5× speed (AVI)In situ TEM movie showing the growth of a Li2O nanorod (corresponding to Figure S6). The Li2O grew directly along the CNT. The movie was recorded at 5 frames/s in TEM bright-field images and played at 34× speed (AVI)In situ TEM movie showing the compression of a Li2O nanorod (corresponding to Figure 3a). The movie was recorded at 5 frames/s in TEM bright-field images and played at 22× speed (AVI)In situ TEM movie showing the compression of a Li2O nanotube (corresponding to Figure 3e). The movie was recorded at 5 frames/s in TEM bright-field images and played at 30× speed (AVI)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology